DuPont Performance Polymers Crastin® SK615SF NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® SK615SF NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Glass Reinforced Low Viscosity Polybutylene Terephthalate Developed for Super Fast Production Crastin SK615SF is a 30% glass fiber reinforced low viscosity polybutylene terephthalate for injection molding. It has high flow characteristics and is spInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
1.54 g/cc
0.0556 lb/in³
ISO 1183
Water Absorption 0.35 %

@Thickness 2.00 mm
 0.35 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %

@Thickness 2.00 mm
 0.150 %

@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 150 MPa
21800 psi
ISO 527-1/-2
Tensile Stress 6.288 MPa

@Strain 0.152378 %,
Temperature 140 °C
 911.9 psi

@Strain 0.152378 %,
Temperature 284 °F
 ISO 11403-1 -2
8.422 MPa

@Strain 0.240189 %,
Temperature 160 °C
 1222 psi

@Strain 0.240189 %,
Temperature 320 °F
 ISO 11403-1 -2
15.15 MPa

@Strain 0.386488 %,
Temperature 140 °C
 2197 psi

@Strain 0.386488 %,
Temperature 284 °F
 ISO 11403-1 -2
15.45 MPa

@Strain 0.143435 %,
Temperature -20.0 °C
 2240 psi

@Strain 0.143435 %,
Temperature -4.00 °F
 ISO 11403-1 -2
15.51 MPa

@Strain 0.141174 %,
Temperature -40.0 °C
 2249 psi

@Strain 0.141174 %,
Temperature -40.0 °F
 ISO 11403-1 -2
16.86 MPa

@Strain 0.210062 %,
Temperature 40.0 °C
 2445 psi

@Strain 0.210062 %,
Temperature 104 °F
 ISO 11403-1 -2
22.62 MPa

@Strain 0.215233 %,
Temperature 23.0 °C
 3281 psi

@Strain 0.215233 %,
Temperature 73.4 °F
 ISO 11403-1 -2
23.28 MPa

@Strain 0.231655 %,
Temperature 0.000 °C
 3377 psi

@Strain 0.231655 %,
Temperature 32.0 °F
 ISO 11403-1 -2
24.29 MPa

@Strain 0.690557 %,
Temperature 140 °C
 3522 psi

@Strain 0.690557 %,
Temperature 284 °F
 ISO 11403-1 -2
30.06 MPa

@Strain 1.37862 %,
Temperature 160 °C
 4360 psi

@Strain 1.37862 %,
Temperature 320 °F
 ISO 11403-1 -2
32.585 MPa

@Strain 1.0723 %,
Temperature 140 °C
 4726.1 psi

@Strain 1.0723 %,
Temperature 284 °F
 ISO 11403-1 -2
34.518 MPa

@Strain 0.453157 %,
Temperature 40.0 °C
 5006.4 psi

@Strain 0.453157 %,
Temperature 104 °F
 ISO 11403-1 -2
36.42 MPa

@Strain 2.02599 %,
Temperature 160 °C
 5282 psi

@Strain 2.02599 %,
Temperature 320 °F
 ISO 11403-1 -2
39.23 MPa

@Strain 2.53541 %,
Temperature 160 °C
 5690 psi

@Strain 2.53541 %,
Temperature 320 °F
 ISO 11403-1 -2
41.66 MPa

@Strain 0.412778 %,
Temperature 23.0 °C
 6043 psi

@Strain 0.412778 %,
Temperature 73.4 °F
 ISO 11403-1 -2
43.48 MPa

@Strain 0.410528 %,
Temperature -20.0 °C
 6307 psi

@Strain 0.410528 %,
Temperature -4.00 °F
 ISO 11403-1 -2
45.36 MPa

@Strain 0.453926 %,
Temperature 0.000 °C
 6579 psi

@Strain 0.453926 %,
Temperature 32.0 °F
 ISO 11403-1 -2
48.77 MPa

@Strain 2.68009 %,
Temperature 140 °C
 7073 psi

@Strain 2.68009 %,
Temperature 284 °F
 ISO 11403-1 -2
52.96 MPa

@Strain 0.746328 %,
Temperature 40.0 °C
 7681 psi

@Strain 0.746328 %,
Temperature 104 °F
 ISO 11403-1 -2
62.36 MPa

@Strain 0.591272 %,
Temperature -40.0 °C
 9045 psi

@Strain 0.591272 %,
Temperature -40.0 °F
 ISO 11403-1 -2
64.57 MPa

@Strain 0.683319 %,
Temperature 23.0 °C
 9365 psi

@Strain 0.683319 %,
Temperature 73.4 °F
 ISO 11403-1 -2
69.31 MPa

@Strain 0.710966 %,
Temperature 0.000 °C
 10050 psi

@Strain 0.710966 %,
Temperature 32.0 °F
 ISO 11403-1 -2
71.131 MPa

@Strain 1.0997 %,
Temperature 40.0 °C
 10317 psi

@Strain 1.0997 %,
Temperature 104 °F
 ISO 11403-1 -2
72.09 MPa

@Strain 0.700638 %,
Temperature -20.0 °C
 10460 psi

@Strain 0.700638 %,
Temperature -4.00 °F
 ISO 11403-1 -2
87.83 MPa

@Strain 1.00996 %,
Temperature 23.0 °C
 12740 psi

@Strain 1.00996 %,
Temperature 73.4 °F
 ISO 11403-1 -2
91.14 MPa

@Strain 0.87993 %,
Temperature -40.0 °C
 13220 psi

@Strain 0.87993 %,
Temperature -40.0 °F
 ISO 11403-1 -2
93.89 MPa

@Strain 1.01022 %,
Temperature 0.000 °C
 13620 psi

@Strain 1.01022 %,
Temperature 32.0 °F
 ISO 11403-1 -2
100.4 MPa

@Strain 1.02518 %,
Temperature -20.0 °C
 14560 psi

@Strain 1.02518 %,
Temperature -4.00 °F
 ISO 11403-1 -2
108.7 MPa

@Strain 2.58789 %,
Temperature 40.0 °C
 15770 psi

@Strain 2.58789 %,
Temperature 104 °F
 ISO 11403-1 -2
121.5 MPa

@Strain 1.21618 %,
Temperature -40.0 °C
 17620 psi

@Strain 1.21618 %,
Temperature -40.0 °F
 ISO 11403-1 -2
174.0 MPa

@Strain 2.41732 %,
Temperature -20.0 °C
 25240 psi

@Strain 2.41732 %,
Temperature -4.00 °F
 ISO 11403-1 -2
Elongation at Break 2.5 %
2.5 %
ISO 527-1/-2
Tensile Modulus 10.0 GPa
1450 ksi
ISO 527-1/-2
Secant Modulus 2.71 GPa

@Strain 2.64148 %,
Temperature 80.0 °C
 393 ksi

@Strain 2.64148 %,
Temperature 176 °F
 ISO 11403-1 -2
2.79 GPa

@Strain 2.08034 %,
Temperature 100 °C
 405 ksi

@Strain 2.08034 %,
Temperature 212 °F
 ISO 11403-1 -2
4.06 GPa

@Strain 1.2473 %,
Temperature 80.0 °C
 589 ksi

@Strain 1.2473 %,
Temperature 176 °F
 ISO 11403-1 -2
4.46 GPa

@Strain 0.591579 %,
Temperature 100 °C
 647 ksi

@Strain 0.591579 %,
Temperature 212 °F
 ISO 11403-1 -2
4.93 GPa

@Strain 0.600598 %,
Temperature 80.0 °C
 715 ksi

@Strain 0.600598 %,
Temperature 176 °F
 ISO 11403-1 -2
5.02 GPa

@Strain 0.229987 %,
Temperature 100 °C
 728 ksi

@Strain 0.229987 %,
Temperature 212 °F
 ISO 11403-1 -2
5.04 GPa

@Strain 1.99815 %,
Temperature 40.0 °C
 731 ksi

@Strain 1.99815 %,
Temperature 104 °F
 ISO 11403-1 -2
5.46 GPa

@Strain 0.294996 %,
Temperature 80.0 °C
 793 ksi

@Strain 0.294996 %,
Temperature 176 °F
 ISO 11403-1 -2
6.01 GPa

@Strain 1.36981 %,
Temperature 40.0 °C
 872 ksi

@Strain 1.36981 %,
Temperature 104 °F
 ISO 11403-1 -2
6.72 GPa

@Strain 1.87532 %,
Temperature 23.0 °C
 974 ksi

@Strain 1.87532 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.8964 GPa

@Strain 0.857481 %,
Temperature 40.0 °C
 1000.3 ksi

@Strain 0.857481 %,
Temperature 104 °F
 ISO 11403-1 -2
7.62 GPa

@Strain 0.453157 %,
Temperature 40.0 °C
 1100 ksi

@Strain 0.453157 %,
Temperature 104 °F
 ISO 11403-1 -2
7.88 GPa

@Strain 1.75077 %,
Temperature 0.000 °C
 1140 ksi

@Strain 1.75077 %,
Temperature 32.0 °F
 ISO 11403-1 -2
8.02 GPa

@Strain 0.210062 %,
Temperature 40.0 °C
 1160 ksi

@Strain 0.210062 %,
Temperature 104 °F
 ISO 11403-1 -2
8.11 GPa

@Strain 1.26111 %,
Temperature 23.0 °C
 1180 ksi

@Strain 1.26111 %,
Temperature 73.4 °F
 ISO 11403-1 -2
8.32 GPa

@Strain 1.822 %,
Temperature -20.0 °C
 1210 ksi

@Strain 1.822 %,
Temperature -4.00 °F
 ISO 11403-1 -2
8.55 GPa

@Strain 2.01539 %,
Temperature -40.0 °C
 1240 ksi

@Strain 2.01539 %,
Temperature -40.0 °F
 ISO 11403-1 -2
8.90 GPa

@Strain 1.23431 %,
Temperature 0.000 °C
 1290 ksi

@Strain 1.23431 %,
Temperature 32.0 °F
 ISO 11403-1 -2
9.21 GPa

@Strain 0.786074 %,
Temperature 23.0 °C
 1340 ksi

@Strain 0.786074 %,
Temperature 73.4 °F
 ISO 11403-1 -2
9.36 GPa

@Strain 1.26922 %,
Temperature -20.0 °C
 1360 ksi

@Strain 1.26922 %,
Temperature -4.00 °F
 ISO 11403-1 -2
9.54 GPa

@Strain 1.4648 %,
Temperature -40.0 °C
 1380 ksi

@Strain 1.4648 %,
Temperature -40.0 °F
 ISO 11403-1 -2
9.62 GPa

@Strain 0.806055 %,
Temperature 0.000 °C
 1400 ksi

@Strain 0.806055 %,
Temperature 32.0 °F
 ISO 11403-1 -2
9.99 GPa

@Strain 0.453926 %,
Temperature 0.000 °C
 1450 ksi

@Strain 0.453926 %,
Temperature 32.0 °F
 ISO 11403-1 -2
10.1 GPa

@Strain 0.231655 %,
Temperature 0.000 °C
 1460 ksi

@Strain 0.231655 %,
Temperature 32.0 °F
 ISO 11403-1 -2
10.1 GPa

@Strain 0.412778 %,
Temperature 23.0 °C
 1460 ksi

@Strain 0.412778 %,
Temperature 73.4 °F
 ISO 11403-1 -2