DuPont Performance Polymers Crastin® SK612SF NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® SK612SF NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)&l.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% Glass Reinforced Low Viscosity Polybutylene Terephthalate Developed for Super Fast Production Crastin SK612SF is a 15% glass fiber reinforced low viscosity polybutylene terephthalate for injection molding. It has high flow characteristics and is spInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
1.42 g/cc
0.0513 lb/in³
ISO 1183
Water Absorption 0.40 %

@Thickness 2.00 mm
0.40 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.150 %

@Thickness 2.00 mm
0.150 %

@Thickness 0.0787 in
Sim. to ISO 62
Viscosity 54480 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
54480 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
ISO 11403-1 -2
65970 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
65970 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
ISO 11403-1 -2
81200 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
81200 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
ISO 11403-1 -2
152700 cP

@Shear Rate 500 1/s,
Temperature 260 °C
152700 cP

@Shear Rate 500 1/s,
Temperature 500 °F
ISO 11403-1 -2
187800 cP

@Shear Rate 500 1/s,
Temperature 250 °C
187800 cP

@Shear Rate 500 1/s,
Temperature 482 °F
ISO 11403-1 -2
234000 cP

@Shear Rate 500 1/s,
Temperature 240 °C
234000 cP

@Shear Rate 500 1/s,
Temperature 464 °F
ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
ISO 527-1/-2
Tensile Stress 9.443 MPa

@Strain 0.546765 %,
Temperature 160 °C
1370 psi

@Strain 0.546765 %,
Temperature 320 °F
ISO 11403-1 -2
10.44 MPa

@Strain 0.543915 %,
Temperature 140 °C
1514 psi

@Strain 0.543915 %,
Temperature 284 °F
ISO 11403-1 -2
13.88 MPa

@Strain 0.298656 %,
Temperature 40.0 °C
2013 psi

@Strain 0.298656 %,
Temperature 104 °F
ISO 11403-1 -2
15.16 MPa

@Strain 0.239814 %,
Temperature -40.0 °C
2198 psi

@Strain 0.239814 %,
Temperature -40.0 °F
ISO 11403-1 -2
15.89 MPa

@Strain 0.268361 %,
Temperature 23.0 °C
2304 psi

@Strain 0.268361 %,
Temperature 73.4 °F
ISO 11403-1 -2
16.44 MPa

@Strain 0.263749 %,
Temperature -20.0 °C
2384 psi

@Strain 0.263749 %,
Temperature -4.00 °F
ISO 11403-1 -2
19.57 MPa

@Strain 1.3907 %,
Temperature 160 °C
2839 psi

@Strain 1.3907 %,
Temperature 320 °F
ISO 11403-1 -2
20.30 MPa

@Strain 0.332444 %,
Temperature 0.000 °C
2945 psi

@Strain 0.332444 %,
Temperature 32.0 °F
ISO 11403-1 -2
20.39 MPa

@Strain 1.23103 %,
Temperature 140 °C
2957 psi

@Strain 1.23103 %,
Temperature 284 °F
ISO 11403-1 -2
25.94 MPa

@Strain 2.21207 %,
Temperature 160 °C
3762 psi

@Strain 2.21207 %,
Temperature 320 °F
ISO 11403-1 -2
28.35 MPa

@Strain 2.01089 %,
Temperature 140 °C
4111 psi

@Strain 2.01089 %,
Temperature 284 °F
ISO 11403-1 -2
30.25 MPa

@Strain 0.682024 %,
Temperature 40.0 °C
4387 psi

@Strain 0.682024 %,
Temperature 104 °F
ISO 11403-1 -2
30.59 MPa

@Strain 3.09033 %,
Temperature 160 °C
4437 psi

@Strain 3.09033 %,
Temperature 320 °F
ISO 11403-1 -2
32.37 MPa

@Strain 0.525841 %,
Temperature -20.0 °C
4695 psi

@Strain 0.525841 %,
Temperature -4.00 °F
ISO 11403-1 -2
32.91 MPa

@Strain 0.527955 %,
Temperature -40.0 °C
4774 psi

@Strain 0.527955 %,
Temperature -40.0 °F
ISO 11403-1 -2
34.51 MPa

@Strain 2.90782 %,
Temperature 140 °C
5006 psi

@Strain 2.90782 %,
Temperature 284 °F
ISO 11403-1 -2
34.73 MPa

@Strain 0.597341 %,
Temperature 23.0 °C
5037 psi

@Strain 0.597341 %,
Temperature 73.4 °F
ISO 11403-1 -2
35.17 MPa

@Strain 0.579891 %,
Temperature 0.000 °C
5101 psi

@Strain 0.579891 %,
Temperature 32.0 °F
ISO 11403-1 -2
46.94 MPa

@Strain 1.13289 %,
Temperature 40.0 °C
6808 psi

@Strain 1.13289 %,
Temperature 104 °F
ISO 11403-1 -2
47.47 MPa

@Strain 0.779352 %,
Temperature -20.0 °C
6886 psi

@Strain 0.779352 %,
Temperature -4.00 °F
ISO 11403-1 -2
49.06 MPa

@Strain 0.795618 %,
Temperature -40.0 °C
7116 psi

@Strain 0.795618 %,
Temperature -40.0 °F
ISO 11403-1 -2
51.90 MPa

@Strain 0.872047 %,
Temperature 0.000 °C
7527 psi

@Strain 0.872047 %,
Temperature 32.0 °F
ISO 11403-1 -2
54.34 MPa

@Strain 0.971766 %,
Temperature 23.0 °C
7881 psi

@Strain 0.971766 %,
Temperature 73.4 °F
ISO 11403-1 -2
62.24 MPa

@Strain 1.66228 %,
Temperature 40.0 °C
9027 psi

@Strain 1.66228 %,
Temperature 104 °F
ISO 11403-1 -2
63.03 MPa

@Strain 1.05428 %,
Temperature -20.0 °C
9142 psi

@Strain 1.05428 %,
Temperature -4.00 °F
ISO 11403-1 -2
64.96 MPa

@Strain 1.07013 %,
Temperature -40.0 °C
9422 psi

@Strain 1.07013 %,
Temperature -40.0 °F
ISO 11403-1 -2
69.141 MPa

@Strain 1.20176 %,
Temperature 0.000 °C
10028 psi

@Strain 1.20176 %,
Temperature 32.0 °F
ISO 11403-1 -2
73.73 MPa

@Strain 1.40132 %,
Temperature 23.0 °C
10690 psi

@Strain 1.40132 %,
Temperature 73.4 °F
ISO 11403-1 -2
107.5 MPa

@Strain 2.00763 %,
Temperature -20.0 °C
15590 psi

@Strain 2.00763 %,
Temperature -4.00 °F
ISO 11403-1 -2
110.99 MPa

@Strain 2.0059 %,
Temperature -40.0 °C
16098 psi

@Strain 2.0059 %,
Temperature -40.0 °F
ISO 11403-1 -2
Elongation at Break 3.3 %
3.3 %
ISO 527-1/-2
Tensile Modulus 6.00 GPa
870 ksi
ISO 527-1/-2
Secant Modulus 1.23 GPa

@Strain 4.12508 %,
Temperature 100 °C
179 ksi

@Strain 4.12508 %,
Temperature 212 °F
ISO 11403-1 -2
1.2757 GPa

@Strain 4.5039 %,
Temperature 80.0 °C
185.03 ksi

@Strain 4.5039 %,
Temperature 176 °F
ISO 11403-1 -2
1.78 GPa

@Strain 2.20401 %,
Temperature 100 °C
258 ksi

@Strain 2.20401 %,
Temperature 212 °F
ISO 11403-1 -2
2.06 GPa

@Strain 2.00926 %,
Temperature 80.0 °C
298 ksi

@Strain 2.00926 %,
Temperature 176 °F
ISO 11403-1 -2
2.20 GPa

@Strain 1.02372 %,
Temperature 100 °C
319 ksi

@Strain 1.02372 %,
Temperature 212 °F
ISO 11403-1 -2
2.3886 GPa

@Strain 1.11375 %,
Temperature 80.0 °C
346.44 ksi

@Strain 1.11375 %,
Temperature 176 °F
ISO 11403-1 -2
2.45 GPa

@Strain 0.411103 %,
Temperature 100 °C
355 ksi

@Strain 0.411103 %,
Temperature 212 °F
ISO 11403-1 -2
2.68 GPa

@Strain 0.437002 %,
Temperature 80.0 °C
388 ksi

@Strain 0.437002 %,
Temperature 176 °F
ISO 11403-1 -2
2.7596 GPa

@Strain 3.00056 %,
Temperature 40.0 °C
400.25 ksi

@Strain 3.00056 %,
Temperature 104 °F
ISO 11403-1 -2
3.43 GPa

@Strain 2.06534 %,
Temperature 40.0 °C
497 ksi

@Strain 2.06534 %,
Temperature 104 °F
ISO 11403-1 -2
4.0227 GPa

@Strain 1.30015 %,
Temperature 40.0 °C
583.45 ksi

@Strain 1.30015 %,
Temperature 104 °F
ISO 11403-1 -2
4.10 GPa

@Strain 2.5045 %,
Temperature 23.0 °C
595 ksi

@Strain 2.5045 %,
Temperature 73.4 °F
ISO 11403-1 -2
4.44 GPa

@Strain 0.682024 %,
Temperature 40.0 °C
643 ksi

@Strain 0.682024 %,
Temperature 104 °F
ISO 11403-1 -2
4.65 GPa

@Strain 0.298656 %,
Temperature 40.0 °C
674 ksi

@Strain 0.298656 %,
Temperature 104 °F
ISO 11403-1 -2
4.97 GPa

@Strain 1.72197 %,
Temperature 23.0 °C
721 ksi

@Strain 1.72197 %,
Temperature 73.4 °F
ISO 11403-1 -2
5.14 GPa

@Strain 1.96921 %,
Temperature 0.000 °C
745 ksi

@Strain 1.96921 %,
Temperature 32.0 °F
ISO 11403-1 -2
5.49 GPa

@Strain 1.11022 %,
Temperature 23.0 °C
796 ksi

@Strain 1.11022 %,
Temperature 73.4 °F
ISO 11403-1 -2
5.59 GPa

@Strain 1.44095 %,
Temperature 0.000 °C
810 ksi

@Strain 1.44095 %,
Temperature 32.0 °F
ISO 11403-1 -2
5.61 GPa

@Strain 1.66598 %,
Temperature -20.0 °C
814 ksi

@Strain 1.66598 %,
Temperature -4.00 °F
ISO 11403-1 -2
5.75 GPa

@Strain 1.67592 %,
Temperature -40.0 °C
833 ksi

@Strain 1.67592 %,
Temperature -40.0 °F
ISO 11403-1 -2