DuPont Performance Polymers Crastin® SK603 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® SK603 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Reinforced Polybutylene Terephthalate Crastin SK603 NC010 is a 20% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.26 g/cc
0.0455 lb/in³
1.45 g/cc
0.0524 lb/in³
ISO 1183
Water Absorption 0.40 %

@Thickness 2.00 mm
 0.40 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.150 %

@Thickness 2.00 mm
 0.150 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 80120 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 80120 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
94280 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 94280 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
112300 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 112300 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
238200 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 238200 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
293100 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 293100 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
362400 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 362400 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 125 MPa
18100 psi
ISO 527-1/-2
Tensile Stress 21.6 MPa

@Strain 0.300 %,
Temperature 23.0 °C
 3130 psi

@Strain 0.300 %,
Temperature 73.4 °F
 ISO 11403-1 -2
73.5 MPa

@Strain 1.20 %,
Temperature 23.0 °C
 10700 psi

@Strain 1.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
105 MPa

@Strain 2.10 %,
Temperature 23.0 °C
 15200 psi

@Strain 2.10 %,
Temperature 73.4 °F
 ISO 11403-1 -2
115 MPa

@Strain 3.30 %,
Temperature 23.0 °C
 16700 psi

@Strain 3.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
10.0 MPa

@Strain 0.152 %,
Time 36000 sec
 1450 psi

@Strain 0.152 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.179 %,
Time 3.60e+6 sec
 1450 psi

@Strain 0.179 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
20.0 MPa

@Strain 0.286 %,
Time 3600 sec
 2900 psi

@Strain 0.286 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
30.0 MPa

@Strain 0.510 %,
Time 360000 sec
 4350 psi

@Strain 0.510 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 0.975 %,
Time 3.60e+6 sec
 7250 psi

@Strain 0.975 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 0.785 %,
Time 36000 sec
 7250 psi

@Strain 0.785 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 0.745 %,
Time 3600 sec
 7250 psi

@Strain 0.745 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
60.0 MPa

@Strain 1.09 %,
Time 360000 sec
 8700 psi

@Strain 1.09 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
Elongation at Break 3.2 %
3.2 %
ISO 527-1/-2
Tensile Modulus 7.40 GPa
1070 ksi
ISO 527-1/-2
2.20 GPa

@Temperature 150 °C
 319 ksi

@Temperature 302 °F
 ISO 11403-1 -2
3.684 GPa

@Temperature 60.0 °C
 534.3 ksi

@Temperature 140 °F
 ISO 11403-1 -2
7.35 GPa

@Temperature -20.0 °C
 1070 ksi

@Temperature -4.00 °F
 ISO 11403-1 -2
Flexural Strength 180 MPa
26100 psi
ISO 178
Flexural Modulus 6.20 GPa
899 ksi
ISO 178
Shear Modulus 0.365 GPa

@Temperature 160 °C
 52.9 ksi

@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.471 GPa

@Temperature 120 °C
 68.3 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.704 GPa

@Temperature 70.0 °C
 102 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
1.54 GPa

@Temperature 20.0 °C
 223 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.66 GPa

@Temperature -20.0 °C
 241 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.77 GPa

@Temperature -50.0 °C
 257 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 4.625 GPa

@Strain 2.40 %,
Temperature 23.0 °C
 670.8 ksi

@Strain 2.40 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.125 GPa

@Strain 1.20 %,
Temperature 23.0 °C
 888.4 ksi

@Strain 1.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
7.20 GPa

@Strain 0.300 %,
Temperature 23.0 °C
 1040 ksi

@Strain 0.300 %,
Temperature 73.4 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 9.00 kJ/m²
4.28 ft-lb/in²
ISO 180/1A
8.00 kJ/m²

@Temperature -30.0 °C
 3.81 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 60.0 kJ/m²
28.6 ft-lb/in²
ISO 180/1U
60.0 kJ/m²

@Temperature -30.0 °C
 28.6 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1U
Charpy Impact Unnotched 6.00 J/cm²
28.6 ft-lb/in²
ISO 179/1eU
5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.800 J/cm²
3.81 ft-lb/in²
ISO 179/1eA
0.900 J/cm²

@Temperature -30.0 °C
 4.28 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 3090 MPa

@Pressure 50.0 MPa,
Temperature 60.0 °C
 448000 psi

@Pressure 7250 psi,
Temperature 140 °F
 ISO 11403-1 -2
3090 MPa

@Pressure 40.0 MPa,
Temperature 60.0 °C
 448000 psi

@Pressure 5800 psi,
Temperature 140 °F
 ISO 11403-1 -2
3100 MPa

@Pressure 30.0 MPa,
Temperature 60.0 °C
 450000 psi

@Pressure 4350 psi,
Temperature 140 °F
 ISO 11403-1 -2
3110 MPa

@Pressure 20.0 MPa,
Temperature 60.0 °C
 451000 psi

@Pressure 2900 psi,
Temperature 140 °F
 ISO 11403-1 -2
3119.7 MPa

@Pressure 10.0 MPa,
Temperature 60.0 °C
 452480 psi

@Pressure 1450 psi,
Temperature 140 °F
 ISO 11403-1 -2
6060 MPa

@Pressure 80.0 MPa,
Temperature 23.0 °C
 879000 psi

@Pressure 11600 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
6310 MPa

@Pressure 70.0 MPa,
Temperature 23.0 °C
 915000 psi

@Pressure 10200 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
6540 MPa

@Pressure 60.0 MPa,
Temperature 23.0 °C
 949000 psi

@Pressure 8700 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
6710 MPa

@Pressure 50.0 MPa,
Temperature 23.0 °C
 973000 psi

@Pressure 7250 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
6840 MPa

@Pressure 40.0 MPa,
Temperature 23.0 °C
 992000 psi

@Pressure 5800 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
6970.9 MPa

@Pressure 10.0 MPa,
Temperature 23.0 °C
 1.0110e+6 psi

@Pressure 1450 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
6980 MPa

@Pressure 30.0 MPa,
Temperature 23.0 °C
 1.01e+6 psi

@Pressure 4350 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
6990 MPa

@Pressure 20.0 MPa,
Temperature 23.0 °C
 1.01e+6 psi

@Pressure 2900 psi,
Temperature 73.4 °F
 ISO 11403-1 -2
7200 MPa

@Time 3600 sec
 1.04e+6 psi

@Time 1.00 hour
 ISO 899-1
Tensile Creep Modulus, 1000 hours 2480 MPa

@Pressure 50.0 MPa,
Temperature 60.0 °C
 359000 psi

@Pressure 7250 psi,
Temperature 140 °F
 ISO 11403-1 -2