DuPont Performance Polymers Crastin® SK602 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® SK602 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
15% Glass Reinforced Polybutylene Terephthalate Crastin SK602 NC010 is a 15% glass fiber reinforced lubricated polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.22 g/cc
0.0441 lb/in³
1.41 g/cc
0.0509 lb/in³
ISO 1183
Water Absorption 0.42 %

@Thickness 2.00 mm
 0.42 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.170 %

@Thickness 2.00 mm
 0.170 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 77750 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 77750 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
90080 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 90080 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
105400 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 105400 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
224600 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 224600 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
274400 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 274400 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
336400 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 336400 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 105 cm³/g
105 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.011 cm/cm
0.011 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 109 MPa
15800 psi
ISO 527-1/-2
Tensile Stress 14.41 MPa

@Strain 0.560 %,
Temperature 90.0 °C
 2090 psi

@Strain 0.560 %,
Temperature 194 °F
 ISO 11403-1 -2
18.07 MPa

@Strain 0.320 %,
Temperature 23.0 °C
 2621 psi

@Strain 0.320 %,
Temperature 73.4 °F
 ISO 11403-1 -2
18.34 MPa

@Strain 0.450 %,
Temperature 40.0 °C
 2660 psi

@Strain 0.450 %,
Temperature 104 °F
 ISO 11403-1 -2
41.62 MPa

@Strain 2.02 %,
Temperature 90.0 °C
 6036 psi

@Strain 2.02 %,
Temperature 194 °F
 ISO 11403-1 -2
52.91 MPa

@Strain 1.54 %,
Temperature 40.0 °C
 7674 psi

@Strain 1.54 %,
Temperature 104 °F
 ISO 11403-1 -2
54.86 MPa

@Strain 3.57 %,
Temperature 90.0 °C
 7957 psi

@Strain 3.57 %,
Temperature 194 °F
 ISO 11403-1 -2
57.84 MPa

@Strain 5.03 %,
Temperature 90.0 °C
 8389 psi

@Strain 5.03 %,
Temperature 194 °F
 ISO 11403-1 -2
67.19 MPa

@Strain 1.30 %,
Temperature 23.0 °C
 9745 psi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
77.38 MPa

@Strain 2.80 %,
Temperature 40.0 °C
 11220 psi

@Strain 2.80 %,
Temperature 104 °F
 ISO 11403-1 -2
83.47 MPa

@Strain 3.88 %,
Temperature 40.0 °C
 12110 psi

@Strain 3.88 %,
Temperature 104 °F
 ISO 11403-1 -2
97.45 MPa

@Strain 2.25 %,
Temperature 23.0 °C
 14130 psi

@Strain 2.25 %,
Temperature 73.4 °F
 ISO 11403-1 -2
108.8 MPa

@Strain 3.23 %,
Temperature 23.0 °C
 15780 psi

@Strain 3.23 %,
Temperature 73.4 °F
 ISO 11403-1 -2
10.0 MPa

@Strain 0.230 %,
Time 3.60e+6 sec
 1450 psi

@Strain 0.230 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.260 %,
Time 3.60e+7 sec
 1450 psi

@Strain 0.260 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.210 %,
Time 360000 sec
 1450 psi

@Strain 0.210 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
20.0 MPa

@Strain 0.360 %,
Time 3600 sec
 2900 psi

@Strain 0.360 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
20.0 MPa

@Strain 0.390 %,
Time 36000 sec
 2900 psi

@Strain 0.390 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 1.03 %,
Time 36000 sec
 7250 psi

@Strain 1.03 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 0.990 %,
Time 3600 sec
 7250 psi

@Strain 0.990 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 1.62 %,
Time 3.60e+7 sec
 7250 psi

@Strain 1.62 %,
Time 10000 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 1.34 %,
Time 3.60e+6 sec
 7250 psi

@Strain 1.34 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 1.16 %,
Time 360000 sec
 7250 psi

@Strain 1.16 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
Elongation at Break 3.5 %
3.5 %
ISO 527-1/-2
Tensile Modulus 5.80 GPa
841 ksi
ISO 527-1/-2
Flexural Strength 160 MPa
23200 psi
ISO 178
Flexural Modulus 5.20 GPa
754 ksi
ISO 178
Shear Modulus 0.328 GPa

@Temperature 160 °C
 47.6 ksi

@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.393 GPa

@Temperature 120 °C
 57.0 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
0.568 GPa

@Temperature 70.0 °C
 82.4 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
1.42 GPa

@Temperature 20.0 °C
 206 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.56 GPa

@Temperature -20.0 °C
 226 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
1.62 GPa

@Temperature -50.0 °C
 235 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 2.56 GPa

@Strain 3.16 %,
Temperature 40.0 °C
 371 ksi

@Strain 3.16 %,
Temperature 104 °F
 ISO 11403-1 -2
3.44 GPa

@Strain 1.54 %,
Temperature 40.0 °C
 498 ksi

@Strain 1.54 %,
Temperature 104 °F
 ISO 11403-1 -2
3.98 GPa

@Strain 2.59 %,
Temperature 23.0 °C
 578 ksi

@Strain 2.59 %,
Temperature 73.4 °F
 ISO 11403-1 -2
4.08 GPa

@Strain 0.450 %,
Temperature 40.0 °C
 591 ksi

@Strain 0.450 %,
Temperature 104 °F
 ISO 11403-1 -2
5.17 GPa

@Strain 1.30 %,
Temperature 23.0 °C
 750 ksi

@Strain 1.30 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.65 GPa

@Strain 0.320 %,
Temperature 23.0 °C
 819 ksi

@Strain 0.320 %,
Temperature 73.4 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 6.50 kJ/m²
3.09 ft-lb/in²
ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
6.00 kJ/m²

@Temperature -40.0 °C
 2.86 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²
23.8 ft-lb/in²
ISO 180/1U
30.0 kJ/m²

@Temperature -40.0 °C
 14.3 ft-lb/in²

@Temperature -40.0 °F
 ISO 180/1U
50.0 kJ/m²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1U
Charpy Impact Unnotched 4.50 J/cm²
21.4 ft-lb/in²
ISO 179/1eU
4.00 J/cm²

@Temperature -40.0 °C
 19.0 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eU
4.50 J/cm²

@Temperature -30.0 °C
 21.4 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
0.700 J/cm²

@Temperature -40.0 °C
 3.33 ft-lb/in²

@Temperature -40.0 °F
 ISO 179/1eA