DuPont Performance Polymers Crastin® SK602 BK851 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 20% Glass Fiber Filled
Manufacturer
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® SK602 BK851 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crastin® SK602 BK851 is a 15% glass fiber reinforced, lubricated, black polybutylene terephthalate resin for injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.41 g/cc
0.0509 lb/in³
ISO 1183
Filler Content 15 %
15 %
Mechanical Properties Metric English Comments
Tensile Strength at Break 102 MPa

@Temperature 23.0 °C
14800 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 3.4 %

@Temperature 23.0 °C
3.4 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 5.70 GPa

@Temperature 23.0 °C
827 ksi

@Temperature 73.4 °F
ISO 527
Izod Impact, Notched (ISO) 5.00 kJ/m²

@Temperature 23.0 °C
2.38 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Charpy Impact Unnotched 4.00 J/cm²

@Temperature 23.0 °C
19.0 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 200 °C
392 °F
ISO 75-1/-2
UL RTI, Electrical 130 °C

@Thickness 3.00 mm
266 °F

@Thickness 0.118 in
UL 746B
130 °C

@Thickness 6.00 mm
266 °F

@Thickness 0.236 in
UL 746B
130 °C

@Thickness 0.750 mm
266 °F

@Thickness 0.0295 in
UL 746B
130 °C

@Thickness 1.50 mm
266 °F

@Thickness 0.0591 in
UL 746B
UL RTI, Mechanical with Impact 115 °C

@Thickness 0.750 mm
239 °F

@Thickness 0.0295 in
UL 746B
115 °C

@Thickness 1.50 mm
239 °F

@Thickness 0.0591 in
UL 746B
115 °C

@Thickness 3.00 mm
239 °F

@Thickness 0.118 in
UL 746B
115 °C

@Thickness 6.00 mm
239 °F

@Thickness 0.236 in
UL 746B
UL RTI, Mechanical without Impact 120 °C

@Thickness 0.750 mm
248 °F

@Thickness 0.0295 in
UL 746B
120 °C

@Thickness 3.00 mm
248 °F

@Thickness 0.118 in
UL 746B
120 °C

@Thickness 1.50 mm
248 °F

@Thickness 0.0591 in
UL 746B
120 °C

@Thickness 6.00 mm
248 °F

@Thickness 0.236 in
UL 746B
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
IEC 60695-11-10
HB

@Thickness 6.00 mm
HB

@Thickness 0.236 in
IEC 60695-11-10
HB

@Thickness 6.00 mm
HB

@Thickness 0.236 in
UL94
HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
UL94
HB

@Thickness 3.00 mm
HB

@Thickness 0.118 in
UL94
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Optimum
240 - 260 °C
464 - 500 °F
Mold Temperature 80.0 °C
176 °F
optimum
30.0 - 130 °C
86.0 - 266 °F
Drying Temperature 110 - 130 °C
230 - 266 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Moisture Content <= 0.040 %
<= 0.040 %
Descriptive Properties Value Comments
Additive Lubricant
Appearance Black Color
Drying Recommended Yes
Features Chemical Resistance, Good
Dimensional Stability, Good
Lubricated
Moisture Absorption, Low
Processability, Good
Stiffness, Good
Strength, Good
Filler Glass fiber reinforcement
Forms Pellets
Generic PBT
Material Status Current
Part Marking Code >PBT-GF15<
ISO 11469
Polymer Family Polyester
Polymer Type PBT
Processing Method Injection Molding
Product Category Glass Reinforced Resins
Region Available - Global Yes
Resin Identification PBT-GF15
ISO 1043
RoHS Compliance Contact Manufacturer
Uses Automotive Applications
General Purpose
Industrial Applications
Parts, Engineering
Parts, Machine/Mechanical
Structural Parts