DuPont Performance Polymers Crastin® LW9020FR NC010 PBT+ASA  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® LW9020FR NC010 PBT+ASA  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Reinforced Flame Retardant Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9020FR NC010 is a 20% glass fiber reinforced flame retardant polybutylene terephthalate blend for injection molding. It has improved surfacInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.36 g/cc
0.0491 lb/in³
1.52 g/cc
0.0549 lb/in³
ISO 1183
Water Absorption 0.78 %

@Thickness 2.00 mm
 0.78 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.230 %

@Thickness 2.00 mm
 0.230 %

@Thickness 0.0787 in
 Sim. to ISO 62
Linear Mold Shrinkage, Flow 0.0040 cm/cm
0.0040 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0080 cm/cm
0.0080 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
ISO 527-1/-2
Tensile Stress 16.22 MPa

@Strain 0.260 %,
Temperature 40.0 °C
 2353 psi

@Strain 0.260 %,
Temperature 104 °F
 ISO 11403-1 -2
17.6 MPa

@Strain 0.400 %,
Temperature 90.0 °C
 2550 psi

@Strain 0.400 %,
Temperature 194 °F
 ISO 11403-1 -2
43.3 MPa

@Strain 0.580 %,
Temperature 23.0 °C
 6280 psi

@Strain 0.580 %,
Temperature 73.4 °F
 ISO 11403-1 -2
46.1 MPa

@Strain 1.62 %,
Temperature 90.0 °C
 6690 psi

@Strain 1.62 %,
Temperature 194 °F
 ISO 11403-1 -2
53.1 MPa

@Strain 2.80 %,
Temperature 90.0 °C
 7700 psi

@Strain 2.80 %,
Temperature 194 °F
 ISO 11403-1 -2
55.58 MPa

@Strain 0.980 %,
Temperature 40.0 °C
 8061 psi

@Strain 0.980 %,
Temperature 104 °F
 ISO 11403-1 -2
76.95 MPa

@Strain 1.14 %,
Temperature 23.0 °C
 11160 psi

@Strain 1.14 %,
Temperature 73.4 °F
 ISO 11403-1 -2
78.69 MPa

@Strain 1.71 %,
Temperature 40.0 °C
 11410 psi

@Strain 1.71 %,
Temperature 104 °F
 ISO 11403-1 -2
97.03 MPa

@Strain 1.71 %,
Temperature 23.0 °C
 14070 psi

@Strain 1.71 %,
Temperature 73.4 °F
 ISO 11403-1 -2
Elongation at Break 2.0 %
2.0 %
ISO 527-1/-2
Tensile Modulus 8.50 GPa
1230 ksi
ISO 527-1/-2
Flexural Strength 155 MPa
22500 psi
ISO 178
Secant Modulus 4.29 GPa

@Strain 1.93 %,
Temperature 40.0 °C
 622 ksi

@Strain 1.93 %,
Temperature 104 °F
 ISO 11403-1 -2
5.30 GPa

@Strain 1.91 %,
Temperature 23.0 °C
 769 ksi

@Strain 1.91 %,
Temperature 73.4 °F
 ISO 11403-1 -2
5.67 GPa

@Strain 0.980 %,
Temperature 40.0 °C
 823 ksi

@Strain 0.980 %,
Temperature 104 °F
 ISO 11403-1 -2
6.24 GPa

@Strain 0.260 %,
Temperature 40.0 °C
 905 ksi

@Strain 0.260 %,
Temperature 104 °F
 ISO 11403-1 -2
6.75 GPa

@Strain 1.14 %,
Temperature 23.0 °C
 979 ksi

@Strain 1.14 %,
Temperature 73.4 °F
 ISO 11403-1 -2
7.47 GPa

@Strain 0.580 %,
Temperature 23.0 °C
 1080 ksi

@Strain 0.580 %,
Temperature 73.4 °F
 ISO 11403-1 -2
Izod Impact, Notched (ISO) 6.00 kJ/m²
2.86 ft-lb/in²
ISO 180/1A
6.00 kJ/m²

@Temperature -30.0 °C
 2.86 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1A
Izod Impact, Unnotched (ISO) 33.0 kJ/m²
15.7 ft-lb/in²
ISO 180/1U
33.0 kJ/m²

@Temperature -30.0 °C
 15.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 180/1U
Charpy Impact Unnotched 4.00 J/cm²
19.0 ft-lb/in²
ISO 179/1eU
3.50 J/cm²

@Temperature -30.0 °C
 16.7 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²
3.33 ft-lb/in²
ISO 179/1eA
0.650 J/cm²

@Temperature -30.0 °C
 3.09 ft-lb/in²

@Temperature -22.0 °F
 ISO 179/1eA
Tensile Creep Modulus, 1 hour 7500 MPa

@Time 3600 sec
 1.09e+6 psi

@Time 1.00 hour
 ISO 899-1
Tensile Creep Modulus, 1000 hours 6000 MPa

@Time 3.60e+6 sec
 870000 psi

@Time 1000 hour
 ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 30.0 µm/m-°C
16.7 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 100 µm/m-°C
55.6 µin/in-°F
ISO 11359-1/-2
Specific Heat Capacity 1.90 J/g-°C
0.454 BTU/lb-°F
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
of melt
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 215 °C
419 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 175 °C
347 °F
ISO 75-1/-2
Flammability, UL94 V-0

@Thickness 1.50 mm
 V-0

@Thickness 0.0591 in
 IEC 60695-11-10
Oxygen Index 27 %
27 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+14 ohm
1.00e+14 ohm
IEC 60093
Dielectric Constant 3.5

@Frequency 1.00e+6 Hz
 3.5

@Frequency 1.00e+6 Hz
 IEC 60250
3.7

@Frequency 100 Hz
 3.7

@Frequency 100 Hz
 IEC 60250
Dielectric Strength 29.0 kV/mm
737 kV/in
IEC 60243-1
20.0 kV/mm

@Thickness 2.00 mm
 508 kV/in

@Thickness 0.0787 in
 Short Time; IEC 60243-1
20.0 kV/mm

@Thickness 2.00 mm
 508 kV/in

@Thickness 0.0787 in
 20s; IEC 60243-1
29.0 kV/mm

@Thickness 1.00 mm
 737 kV/in

@Thickness 0.0394 in
 Short Time; IEC 60243-1
Dissipation Factor 0.0030

@Frequency 100 Hz
 0.0030

@Frequency 100 Hz
 IEC 60250
0.0030

@Frequency 100 Hz
 0.0030

@Frequency 100 Hz
 ASTM D150
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 IEC 60250
0.015

@Frequency 1.00e+6 Hz
 0.015

@Frequency 1.00e+6 Hz
 ASTM D150
Comparative Tracking Index 300 V
300 V
IEC 60112
Descriptive Properties Value Comments
Additives Release agent
Delivery Form Pellets
Part Marking Code >PBT+ASA-GF20FR(17)<
ISO 11469
Processing Injection Moulding
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification PBT+ASA-GF20FR(17)
UL recognition UL