DuPont Performance Polymers Crastin® LW9020 NC010 PBT+ASA  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , PBT + ASA Blend, Glass Fiber Reinforced
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® LW9020 NC010 PBT+ASA  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
20% Glass Reinforced Polybutylene Terephthalate Blend with Low Warpage Characteristics Crastin LW9020 NC010 is a 20% glass fiber reinforced polybutylene terephthalate blend for injection molding. It has improved surface aesthetics excellent dimensionalInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.19 g/cc
0.0430 lb/in³
1.35 g/cc
0.0488 lb/in³
ISO 1183
Water Absorption 0.78 %

@Thickness 2.00 mm
 0.78 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.260 %

@Thickness 2.00 mm
 0.260 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 64000 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 64000 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
72000 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 72000 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
83000 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 83000 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
253000 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 253000 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
292000 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 292000 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
338000 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 338000 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4 2577
Mechanical Properties Metric English Comments
Tensile Strength at Break 110 MPa
16000 psi
ISO 527-1/-2
Tensile Stress 2.32 MPa

@Strain 0.250 %,
Temperature 160 °C
 336 psi

@Strain 0.250 %,
Temperature 320 °F
 ISO 11403-1 -2
9.90 MPa

@Strain 1.50 %,
Temperature 160 °C
 1440 psi

@Strain 1.50 %,
Temperature 320 °F
 ISO 11403-1 -2
13.2 MPa

@Strain 3.20 %,
Temperature 160 °C
 1910 psi

@Strain 3.20 %,
Temperature 320 °F
 ISO 11403-1 -2
15.6 MPa

@Strain 0.250 %,
Temperature 40.0 °C
 2260 psi

@Strain 0.250 %,
Temperature 104 °F
 ISO 11403-1 -2
17.5 MPa

@Strain 0.250 %,
Temperature 23.0 °C
 2540 psi

@Strain 0.250 %,
Temperature 73.4 °F
 ISO 11403-1 -2
18.9 MPa

@Strain 0.250 %,
Temperature 0.000 °C
 2740 psi

@Strain 0.250 %,
Temperature 32.0 °F
 ISO 11403-1 -2
19.3 MPa

@Strain 0.250 %,
Temperature -20.0 °C
 2800 psi

@Strain 0.250 %,
Temperature -4.00 °F
 ISO 11403-1 -2
19.8 MPa

@Strain 0.250 %,
Temperature -40.0 °C
 2870 psi

@Strain 0.250 %,
Temperature -40.0 °F
 ISO 11403-1 -2
75.3 MPa

@Strain 1.50 %,
Temperature 40.0 °C
 10900 psi

@Strain 1.50 %,
Temperature 104 °F
 ISO 11403-1 -2
87.7 MPa

@Strain 1.50 %,
Temperature 23.0 °C
 12700 psi

@Strain 1.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
94.9 MPa

@Strain 3.20 %,
Temperature 40.0 °C
 13800 psi

@Strain 3.20 %,
Temperature 104 °F
 ISO 11403-1 -2
97.7 MPa

@Strain 1.50 %,
Temperature 0.000 °C
 14200 psi

@Strain 1.50 %,
Temperature 32.0 °F
 ISO 11403-1 -2
103 MPa

@Strain 1.50 %,
Temperature -20.0 °C
 14900 psi

@Strain 1.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
106 MPa

@Strain 1.50 %,
Temperature -40.0 °C
 15400 psi

@Strain 1.50 %,
Temperature -40.0 °F
 ISO 11403-1 -2
120 MPa

@Strain 3.20 %,
Temperature 23.0 °C
 17400 psi

@Strain 3.20 %,
Temperature 73.4 °F
 ISO 11403-1 -2
10.0 MPa

@Strain 0.207 %,
Time 3.60e+6 sec
 1450 psi

@Strain 0.207 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.150 %,
Time 3600 sec
 1450 psi

@Strain 0.150 %,
Time 1.00 hour
 isochronous; ISO 11403-1 -2
10.0 MPa

@Strain 0.169 %,
Time 36000 sec
 1450 psi

@Strain 0.169 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
20.0 MPa

@Strain 0.380 %,
Time 360000 sec
 2900 psi

@Strain 0.380 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
50.0 MPa

@Strain 0.875 %,
Time 36000 sec
 7250 psi

@Strain 0.875 %,
Time 10.0 hour
 isochronous; ISO 11403-1 -2
60.0 MPa

@Strain 1.22 %,
Time 360000 sec
 8700 psi

@Strain 1.22 %,
Time 100 hour
 isochronous; ISO 11403-1 -2
60.0 MPa

@Strain 1.35 %,
Time 3.60e+6 sec
 8700 psi

@Strain 1.35 %,
Time 1000 hour
 isochronous; ISO 11403-1 -2
70.0 MPa

@Time 3600 sec,
Strain 1.15 %
 10200 psi

@Time 1.00 hour,
Strain 1.15 %
 isochronous; ISO 11403-1 -2
Elongation at Break 2.9 %
2.9 %
ISO 527-1/-2
Tensile Modulus 7.00 GPa
1020 ksi
ISO 527-1/-2
1.124 GPa

@Temperature 145 °C
 163.0 ksi

@Temperature 293 °F
 Dynamic; ISO 11403-1 -2
4.482 GPa

@Temperature 85.0 °C
 650.1 ksi

@Temperature 185 °F
 Dynamic; ISO 11403-1 -2
6.026 GPa

@Temperature 55.0 °C
 874.0 ksi

@Temperature 131 °F
 Dynamic; ISO 11403-1 -2
7.344 GPa

@Temperature 15.0 °C
 1065 ksi

@Temperature 59.0 °F
 Dynamic; ISO 11403-1 -2
7.634 GPa

@Temperature -10.0 °C
 1107 ksi

@Temperature 14.0 °F
 Dynamic; ISO 11403-1 -2
7.75 GPa

@Temperature -35.0 °C
 1120 ksi

@Temperature -31.0 °F
 Dynamic; ISO 11403-1 -2
7.787 GPa

@Temperature -50.0 °C
 1129 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Flexural Strength 170 MPa
24700 psi
ISO 178
Flexural Modulus 6.30 GPa
914 ksi
ISO 178
Shear Modulus 0.210 GPa

@Temperature 160 °C
 30.5 ksi

@Temperature 320 °F
 Dynamic; ISO 11403-1 -2
0.640 GPa

@Temperature 120 °C
 92.8 ksi

@Temperature 248 °F
 Dynamic; ISO 11403-1 -2
1.15 GPa

@Temperature 70.0 °C
 167 ksi

@Temperature 158 °F
 Dynamic; ISO 11403-1 -2
1.81 GPa

@Temperature 20.0 °C
 263 ksi

@Temperature 68.0 °F
 Dynamic; ISO 11403-1 -2
1.92 GPa

@Temperature -20.0 °C
 278 ksi

@Temperature -4.00 °F
 Dynamic; ISO 11403-1 -2
2.14 GPa

@Temperature -50.0 °C
 310 ksi

@Temperature -58.0 °F
 Dynamic; ISO 11403-1 -2
Secant Modulus 2.39 GPa

@Strain 1.50 %,
Temperature 100 °C
 346 ksi

@Strain 1.50 %,
Temperature 212 °F
 ISO 11403-1 -2
3.276 GPa

@Strain 0.250 %,
Temperature 100 °C
 475.2 ksi

@Strain 0.250 %,
Temperature 212 °F
 ISO 11403-1 -2
3.42 GPa

@Strain 1.50 %,
Temperature 80.0 °C
 496 ksi

@Strain 1.50 %,
Temperature 176 °F
 ISO 11403-1 -2
4.56 GPa

@Strain 0.250 %,
Temperature 80.0 °C
 661 ksi

@Strain 0.250 %,
Temperature 176 °F
 ISO 11403-1 -2
5.02 GPa

@Strain 1.50 %,
Temperature 40.0 °C
 728 ksi

@Strain 1.50 %,
Temperature 104 °F
 ISO 11403-1 -2
5.85 GPa

@Strain 1.50 %,
Temperature 23.0 °C
 848 ksi

@Strain 1.50 %,
Temperature 73.4 °F
 ISO 11403-1 -2
6.24 GPa

@Strain 0.250 %,
Temperature 40.0 °C
 905 ksi

@Strain 0.250 %,
Temperature 104 °F
 ISO 11403-1 -2
6.51 GPa

@Strain 1.50 %,
Temperature 0.000 °C
 945 ksi

@Strain 1.50 %,
Temperature 32.0 °F
 ISO 11403-1 -2
6.87 GPa

@Strain 1.50 %,
Temperature -20.0 °C
 996 ksi

@Strain 1.50 %,
Temperature -4.00 °F
 ISO 11403-1 -2
7.00 GPa

@Strain 0.250 %,
Temperature 23.0 °C
 1020 ksi

@Strain 0.250 %,
Temperature 73.4 °F
 ISO 11403-1 -2
7.07 GPa

@Strain 1.50 %,
Temperature -40.0 °C
 1020 ksi

@Strain 1.50 %,
Temperature -40.0 °F
 ISO 11403-1 -2
7.56 GPa

@Strain 0.250 %,
Temperature 0.000 °C
 1100 ksi

@Strain 0.250 %,
Temperature 32.0 °F
 ISO 11403-1 -2