DuPont Performance Polymers Crastin® HR5330HF BK503 PBT  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) , Polybutylene Terephthalate (PBT), 30% Glass Fiber Filled
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® HR5330HF BK503 PBT  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Crastin® HR5330HF is a 30% glass reinforced PBT with high flow (HF), moderately toughened, hydrolysis resistant (HR) resin. Excellent balance of properties between terminal pullout and impact resistance. Developed for USCAR Class 3 and 4 environments.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.50 g/cc
0.0542 lb/in³
ISO 1183
Filler Content 30 %
30 %
Linear Mold Shrinkage, Flow 0.0030 cm/cm

@Thickness 2.00 mm
0.0030 in/in

@Thickness 0.0787 in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.010 cm/cm

@Thickness 2.00 mm
0.010 in/in

@Thickness 0.0787 in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength at Break 120 MPa

@Temperature 23.0 °C
17400 psi

@Temperature 73.4 °F
ISO 527
Elongation at Break 3.5 %

@Temperature 23.0 °C
3.5 %

@Temperature 73.4 °F
ISO 527
Tensile Modulus 8.40 GPa

@Temperature 23.0 °C
1220 ksi

@Temperature 73.4 °F
ISO 527
Flexural Modulus 7.50 GPa

@Temperature 23.0 °C
1090 ksi

@Temperature 73.4 °F
ISO 178
Izod Impact, Notched (ISO) 8.00 kJ/m²

@Temperature -40.0 °C
3.81 ft-lb/in²

@Temperature -40.0 °F
ISO 180/1A
12.0 kJ/m²

@Temperature 23.0 °C
5.71 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1A
Izod Impact, Unnotched (ISO) 50.0 kJ/m²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
ISO 180/1U
Charpy Impact Unnotched 6.50 J/cm²

@Temperature 23.0 °C
30.9 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 0.900 J/cm²

@Temperature -30.0 °C
4.28 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
1.10 J/cm²

@Temperature 23.0 °C
5.23 ft-lb/in²

@Temperature 73.4 °F
ISO 179/1eA
Thermal Properties Metric English Comments
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 221 °C
430 °F
ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 207 °C
405 °F
ISO 75-1/-2
Flammability, UL94 HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
IEC 60695-11-10
HB

@Thickness 0.750 mm
HB

@Thickness 0.0295 in
UL94
Processing Properties Metric English Comments
Melt Temperature 250 °C
482 °F
Optimum
240 - 260 °C
464 - 500 °F
Mold Temperature 80.0 °C
176 °F
optimum
30.0 - 130 °C
86.0 - 266 °F
Drying Temperature 110 - 130 °C
230 - 266 °F
Dry Time 2.00 - 4.00 hour
2.00 - 4.00 hour
Moisture Content <= 0.040 %
<= 0.040 %
Descriptive Properties Value Comments
Additive Hydrolysis Resistant
Lubricant
Appearance Black Color
Drying Recommended Yes
Features Chemical Resistance, Good
Dimensional Stability, Good
Flow, High
Hydrolysis Resistant
Moisture Absorption, Low
Processability, Good
Viscosity, Low
Filler Glass fiber reinforcement
Forms Pellets
Generic PBT
Material Status Current
Part Marking Code >PBT-IGF30<
ISO 11469
Polymer Family Polyester
Polymer Type PBT
Processing Method Injection Molding
Product Category Glass Reinforced Resins
Hydrolysis Resistant Resins
Region Available - Global Yes
Resin Identification PBT-IGF30
ISO 1043
RoHS Compliance Contact Manufacturer
Uses Automotive Applications
Connectors
Electrical/Electronic Applications
Industrial Applications
Parts, Engineering
Parts, Industrial
Parts, Machine/Mechanical