DuPont Performance Polymers Crastin® FG6130 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)<

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® FG6130 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)<.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced High Viscosity Polybutylene Terephthalate Developed for Food Contact Applications and Extrusion and Injection Molding Crastin FG6130 NC010 is an unreinforced medium high viscosity polybutylene terephthalate resin for extrusion and injectioInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
1.30 g/cc
0.0470 lb/in³
ISO 1183
Water Absorption 0.40 %

@Thickness 2.00 mm
0.40 %

@Thickness 0.0787 in
Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
0.200 %

@Thickness 0.0787 in
Sim. to ISO 62
Viscosity Test 130 cm³/g
130 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Melt Flow 15.4 g/10 min

@Load 2.16 kg,
Temperature 250 °C
15.4 g/10 min

@Load 4.76 lb,
Temperature 482 °F
ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength, Yield 59.0 MPa
8560 psi
ISO 527-1/-2
Elongation at Break 50 %
50 %
Nominal; ISO 527-1/-2
Elongation at Yield 8.0 %
8.0 %
ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
Izod Impact, Notched (ISO) 4.00 kJ/m²
1.90 ft-lb/in²
ISO 180/1A
Charpy Impact Unnotched NB
NB
ISO 179/1eU
NB

@Temperature -30.0 °C
NB

@Temperature -22.0 °F
ISO 179/1eU
Charpy Impact, Notched 0.500 J/cm²
2.38 ft-lb/in²
ISO 179/1eA
0.450 J/cm²

@Temperature -30.0 °C
2.14 ft-lb/in²

@Temperature -22.0 °F
ISO 179/1eA
Tensile Creep Modulus, 1 hour 2500 MPa

@Time 3600 sec
363000 psi

@Time 1.00 hour
ISO 899-1
Tensile Creep Modulus, 1000 hours 1800 MPa

@Time 3.60e+6 sec
261000 psi

@Time 1000 hour
ISO 899-1
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 108 µm/m-°C
60.0 µin/in-°F
ISO 11359-1/-2
CTE, linear, Transverse to Flow 144 µm/m-°C
80.0 µin/in-°F
ISO 11359-1/-2
Specific Heat Capacity 2.05 J/g-°C
0.490 BTU/lb-°F
Thermal Conductivity 0.250 W/m-K
1.74 BTU-in/hr-ft²-°F
of melt
Melting Point 225 °C
437 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi) 115 °C
239 °F
ISO 75-1/-2
180 °C
356 °F
annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi) 50.0 °C
122 °F
ISO 75-1/-2
60.0 °C
140 °F
annealed; ISO 75-1/-2
Vicat Softening Point 175 °C
347 °F
50°C/h 50N; ISO 306
Flammability, UL94 HB

@Thickness 1.50 mm
HB

@Thickness 0.0591 in
IEC 60695-11-10
HB

@Thickness 0.800 mm
HB

@Thickness 0.0315 in
IEC 60695-11-10
Oxygen Index 22 %
22 %
ISO 4589-1/-2
Electrical Properties Metric English Comments
Volume Resistivity >= 1.00e+15 ohm-cm
>= 1.00e+15 ohm-cm
IEC 60093
Surface Resistance 1.00e+12 ohm
1.00e+12 ohm
IEC 60093
Dielectric Strength 26.0 kV/mm
660 kV/in
IEC 60243-1
Comparative Tracking Index 600 V
600 V
IEC 60112
Descriptive Properties Value Comments
Delivery Form Pellets
Part Marking Code >PBT<
ISO 11469
Processing Coatable
Film Extrusion
Injection Moulding
Other Extrusion
Profile Extrusion
Sheet Extrusion
Regional Availability Asia Pacific
Europe
Global
Near East/Africa
North America
South and Central America
Resin Identification PBT
UL recognition UL