- DuPont Performance Polymers Crastin® FG6129 NC010 PBT (Unverified Data**)
DuPont Performance Polymers Crastin® FG6129 NC010 PBT (Unverified Data**)
| Category | Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT) |
| Manufacturer | |
| Trade Name | |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | DuPont Performance Polymers Crastin® FG6129 NC010 PBT
(Unverified Data**).pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Crastin® FG6129 NC010 is an unreinforced, high viscosity polybutylene terephthalate resin for extrusion and injection molding. It has been developed for consideration into applications such as parts for the food industry.Information provided by DuPont Performance Polymers
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.30 g/cc | 0.0470 lb/in³ | ISO 1183 |
| Water Absorption | 0.20 % @Temperature 23.0 °C |
0.20 % @Temperature 73.4 °F |
Equilibrium 50%RH; ISO 62, Similar to |
| 0.40 % @Temperature 23.0 °C |
0.40 % @Temperature 73.4 °F |
Saturation, immersed; ISO 62, Similar to | |
| Linear Mold Shrinkage, Flow | 0.017 cm/cm @Thickness 2.00 mm |
0.017 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.015 cm/cm @Thickness 2.00 mm |
0.015 in/in @Thickness 0.0787 in |
ISO 294-4 |
| Melt Flow | 10 g/10 min @Load 2.16 kg, Temperature 250 °C |
10 g/10 min @Load 4.76 lb, Temperature 482 °F |
ISO 1133 |
| Melt Index of Compound | 10 g/10 min | 10 g/10 min | cm3/10 min; ISO 1133 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 58.0 MPa @Temperature 23.0 °C |
8410 psi @Temperature 73.4 °F |
ISO 527 |
| Elongation at Break | >= 50 % @Temperature 23.0 °C |
>= 50 % @Temperature 73.4 °F |
nominal; ISO 527 |
| 200 % @Temperature 23.0 °C |
200 % @Temperature 73.4 °F |
50mm/min; ISO 527 | |
| Elongation at Yield | 5.0 % @Temperature 23.0 °C |
5.0 % @Temperature 73.4 °F |
ISO 527 |
| Tensile Modulus | 2.60 GPa @Temperature 23.0 °C |
377 ksi @Temperature 73.4 °F |
ISO 527 |
| Flexural Strength | 85.0 MPa @Temperature 23.0 °C |
12300 psi @Temperature 73.4 °F |
ISO 178 |
| Flexural Modulus | 2.35 GPa @Temperature 23.0 °C |
341 ksi @Temperature 73.4 °F |
ISO 178 |
| Izod Impact, Notched (ISO) | 4.50 kJ/m² @Temperature 23.0 °C |
2.14 ft-lb/in² @Temperature 73.4 °F |
ISO 180/1A |
| 6.00 kJ/m² @Temperature -30.0 °C |
2.86 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1A | |
| Izod Impact, Unnotched (ISO) | 130 kJ/m² @Temperature -30.0 °C |
61.9 ft-lb/in² @Temperature -22.0 °F |
ISO 180/1U |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 180/1U | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C |
NB @Temperature -22.0 °F |
ISO 179/1eU |
| NB @Temperature 23.0 °C |
NB @Temperature 73.4 °F |
ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C |
1.90 ft-lb/in² @Temperature -22.0 °F |
ISO 179/1eA |
| 0.550 J/cm² @Temperature 23.0 °C |
2.62 ft-lb/in² @Temperature 73.4 °F |
ISO 179/1eA | |
| Tensile Creep Modulus, 1 hour | 2600 MPa @Temperature 23.0 °C |
377000 psi @Temperature 73.4 °F |
ISO 899 |
| Tensile Creep Modulus, 1000 hours | 1800 MPa @Temperature 23.0 °C |
261000 psi @Temperature 73.4 °F |
ISO 899 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C |
278 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 |
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C |
278 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| 500 µm/m-°C @Temperature 55.0 - 160 °C |
278 µin/in-°F @Temperature 131 - 320 °F |
ISO 11359-1/-2 | |
| CTE, linear, Transverse to Flow | 90.0 µm/m-°C @Temperature -40.0 - 23.0 °C |
50.0 µin/in-°F @Temperature -40.0 - 73.4 °F |
ISO 11359-1/-2 |
| 130 µm/m-°C @Temperature 23.0 - 55.0 °C |
72.2 µin/in-°F @Temperature 73.4 - 131 °F |
ISO 11359-1/-2 | |
| 162 µm/m-°C @Temperature 55.0 - 160 °C |
90.0 µin/in-°F @Temperature 131 - 320 °F |
ISO 11359-1/-2 | |
| Melting Point | 225 °C | 437 °F | 10°C/min; ISO 11357-1/-3 |
| Deflection Temperature at 0.46 MPa (66 psi) | 115 °C | 239 °F | ISO 75-1/-2 |
| 180 °C | 356 °F | Annealed; ISO 75-1/-2 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| 60.0 °C | 140 °F | Annealed; ISO 75-1/-2 |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Temperature | 250 °C | 482 °F | Optimum |
| 240 - 260 °C | 464 - 500 °F | ||
| Mold Temperature | 80.0 °C | 176 °F | optimum |
| 30.0 - 130 °C | 86.0 - 266 °F | ||
| Drying Temperature | 110 - 130 °C | 230 - 266 °F | |
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |
| Moisture Content | <= 0.040 % | <= 0.040 % |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | Natural Color | |
| Features | Food Contact Acceptable | |
| Lubricated | ||
| Viscosity, Low | ||
| Forms | Pellets | |
| Generic | PBT | |
| Material Status | Current | |
| Part Marking Code | >PBT< | ISO 11469 |
| Processing Method | Extrusion | |
| Product Category | Extrusion Resins | |
| Food Contact Resins | ||
| Food Contact Resins | ||
| Unreinforced Resins | ||
| Region Available - Global | Yes | |
| Resin Identification | PBT | ISO 1043 |
| RoHS Compliance | Contact Manufacturer | |
| Uses | Food Applications, Non-specific |