DuPont Performance Polymers Crastin® 6134 NC010 PBT (Unverified Data**)

Category	Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	DuPont Performance Polymers Crastin® 6134 NC010 PBT (Unverified Data**).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

Crastin® 6134 NC010 is an unreinforced, medium viscosity polybutylene terephthalate resin for extrusion and injection molding.Information provided by DuPont Performance Polymers

Physical Properties	Metric	English	Comments
Density	1.30 g/cc	0.0470 lb/in³	ISO 1183
Melt Flow	33 g/10 min @Load 2.16 kg, Temperature 250 °C	33 g/10 min @Load 4.76 lb, Temperature 482 °F	ISO 1133
	33.5 g/10 min @Load 2.16 kg, Temperature 250 °C	33.5 g/10 min @Load 4.76 lb, Temperature 482 °F	ISO 1133

Mechanical Properties	Metric	English	Comments
Tensile Strength, Yield	59.0 MPa @Temperature 23.0 °C	8560 psi @Temperature 73.4 °F	ISO 527
Elongation at Break	45 % @Temperature 23.0 °C	45 % @Temperature 73.4 °F	nominal; ISO 527
	90 % @Temperature 23.0 °C	90 % @Temperature 73.4 °F	50mm/min; ISO 527
Elongation at Yield	4.0 % @Temperature 23.0 °C	4.0 % @Temperature 73.4 °F	ISO 527
Tensile Modulus	2.60 GPa @Temperature 23.0 °C	377 ksi @Temperature 73.4 °F	ISO 527
Flexural Strength	85.0 MPa @Temperature 23.0 °C	12300 psi @Temperature 73.4 °F	ISO 178
Izod Impact, Notched (ISO)	3.50 kJ/m² @Temperature 23.0 °C	1.67 ft-lb/in² @Temperature 73.4 °F	ISO 180/1A
Charpy Impact, Notched	0.400 J/cm² @Temperature 23.0 °C	1.90 ft-lb/in² @Temperature 73.4 °F	ISO 179/1eA

Thermal Properties	Metric	English	Comments
Melting Point	225 °C	437 °F	10°C/min; ISO 11357-1/-3
Deflection Temperature at 0.46 MPa (66 psi)	115 °C	239 °F	ISO 75-1/-2
	180 °C	356 °F	Annealed; ISO 75-1/-2
Deflection Temperature at 1.8 MPa (264 psi)	50.0 °C	122 °F	ISO 75-1/-2
	60.0 °C	140 °F	Annealed; ISO 75-1/-2
Oxygen Index	22 %	22 %	ISO 4589-1/-2

Processing Properties	Metric	English	Comments
Melt Temperature	250 °C	482 °F	Optimum
	240 - 260 °C	464 - 500 °F
Mold Temperature	80.0 °C	176 °F	optimum
	30.0 - 130 °C	86.0 - 266 °F
Drying Temperature	110 - 130 °C	230 - 266 °F
Dry Time	2.00 - 4.00 hour	2.00 - 4.00 hour
Moisture Content	<= 0.040 %	<= 0.040 %

Descriptive Properties	Value	Comments
Appearance	Natural Color
Drying Recommended	Yes
Features	Chemical Resistance, Good
	Dimensional Stability, Good
	Flow, High
	Moisture Absorption, Low
	Processability, Good
	Viscosity, Low
Forms	Pellets
Generic	PBT
Material Status	Current
Part Marking Code	>PBT<	ISO 11469
Processing Method	Extrusion
	Injection Molding
	Injection Molding
Product Category	Extrusion Resins
	Unreinforced Resins
Resin Identification	PBT	ISO 1043
RoHS Compliance	Contact Manufacturer
Uses	Parts, Thin-walled