DuPont Performance Polymers Crastin® 6130 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® 6130 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced High Viscosity Polybutylene Terephthalate Developed for Extrusion and Injection Molding Crastin 6130 NC010 is an unreinforced medium high viscosity polybutylene terephthalate resin for extrusion and injection molding.Information provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.11 g/cc
0.0401 lb/in³
1.30 g/cc
0.0470 lb/in³
ISO 1183
Viscosity 102200 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 102200 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
113100 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 113100 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
125300 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 125300 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
308900 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 308900 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
378000 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 378000 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
436500 cP

@Shear Rate 10.0 1/s,
Temperature 260 °C
 436500 cP

@Shear Rate 10.0 1/s,
Temperature 500 °F
 ISO 11403-1 -2
461700 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 461700 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
582500 cP

@Shear Rate 10.0 1/s,
Temperature 250 °C
 582500 cP

@Shear Rate 10.0 1/s,
Temperature 482 °F
 ISO 11403-1 -2
794600 cP

@Shear Rate 10.0 1/s,
Temperature 240 °C
 794600 cP

@Shear Rate 10.0 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 130 cm³/g
130 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.016 cm/cm
0.016 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Melt Flow 15.4 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 15.4 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 0.410 MPa

@Strain 0.170 %,
Temperature 150 °C
 59.5 psi

@Strain 0.170 %,
Temperature 302 °F
 ISO 11403-1 -2
0.680 MPa

@Strain 0.170 %,
Temperature 90.0 °C
 98.6 psi

@Strain 0.170 %,
Temperature 194 °F
 ISO 11403-1 -2
4.10 MPa

@Strain 2.28 %,
Temperature 150 °C
 595 psi

@Strain 2.28 %,
Temperature 302 °F
 ISO 11403-1 -2
6.67 MPa

@Strain 4.80 %,
Temperature 150 °C
 967 psi

@Strain 4.80 %,
Temperature 302 °F
 ISO 11403-1 -2
7.25 MPa

@Strain 2.25 %,
Temperature 90.0 °C
 1050 psi

@Strain 2.25 %,
Temperature 194 °F
 ISO 11403-1 -2
8.25 MPa

@Strain 7.41 %,
Temperature 150 °C
 1200 psi

@Strain 7.41 %,
Temperature 302 °F
 ISO 11403-1 -2
12.07 MPa

@Strain 4.64 %,
Temperature 90.0 °C
 1751 psi

@Strain 4.64 %,
Temperature 194 °F
 ISO 11403-1 -2
13.63 MPa

@Strain 0.430 %,
Temperature -40.0 °C
 1977 psi

@Strain 0.430 %,
Temperature -40.0 °F
 ISO 11403-1 -2
14.34 MPa

@Strain 1.27 %,
Temperature 40.0 °C
 2080 psi

@Strain 1.27 %,
Temperature 104 °F
 ISO 11403-1 -2
15.07 MPa

@Strain 7.13 %,
Temperature 90.0 °C
 2186 psi

@Strain 7.13 %,
Temperature 194 °F
 ISO 11403-1 -2
16.61 MPa

@Strain 0.700 %,
Temperature 23.0 °C
 2409 psi

@Strain 0.700 %,
Temperature 73.4 °F
 ISO 11403-1 -2
22.95 MPa

@Strain 0.820 %,
Temperature -20.0 °C
 3329 psi

@Strain 0.820 %,
Temperature -4.00 °F
 ISO 11403-1 -2
24.96 MPa

@Strain 3.64 %,
Temperature 40.0 °C
 3620 psi

@Strain 3.64 %,
Temperature 104 °F
 ISO 11403-1 -2
27.2 MPa

@Strain 1.04 %,
Temperature 0.000 °C
 3950 psi

@Strain 1.04 %,
Temperature 32.0 °F
 ISO 11403-1 -2
29.39 MPa

@Strain 6.18 %,
Temperature 40.0 °C
 4263 psi

@Strain 6.18 %,
Temperature 104 °F
 ISO 11403-1 -2
32.22 MPa

@Strain 8.75 %,
Temperature 40.0 °C
 4673 psi

@Strain 8.75 %,
Temperature 104 °F
 ISO 11403-1 -2
45.2 MPa

@Strain 2.17 %,
Temperature 23.0 °C
 6560 psi

@Strain 2.17 %,
Temperature 73.4 °F
 ISO 11403-1 -2
48.4 MPa

@Strain 1.69 %,
Temperature -40.0 °C
 7020 psi

@Strain 1.69 %,
Temperature -40.0 °F
 ISO 11403-1 -2
51.39 MPa

@Strain 2.00 %,
Temperature -20.0 °C
 7454 psi

@Strain 2.00 %,
Temperature -4.00 °F
 ISO 11403-1 -2
54.78 MPa

@Strain 2.40 %,
Temperature 0.000 °C
 7945 psi

@Strain 2.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
65.05 MPa

@Strain 4.22 %,
Temperature 0.000 °C
 9435 psi

@Strain 4.22 %,
Temperature 32.0 °F
 ISO 11403-1 -2
70.55 MPa

@Strain 3.31 %,
Temperature -20.0 °C
 10230 psi

@Strain 3.31 %,
Temperature -4.00 °F
 ISO 11403-1 -2
71.25 MPa

@Strain 2.81 %,
Temperature -40.0 °C
 10330 psi

@Strain 2.81 %,
Temperature -40.0 °F
 ISO 11403-1 -2
77.04 MPa

@Strain 5.18 %,
Temperature -20.0 °C
 11170 psi

@Strain 5.18 %,
Temperature -4.00 °F
 ISO 11403-1 -2
87.67 MPa

@Strain 4.16 %,
Temperature -40.0 °C
 12720 psi

@Strain 4.16 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 59.0 MPa
8560 psi
ISO 527-1/-2
Elongation at Break 50 %
50 %
Nominal; ISO 527-1/-2
Elongation at Yield 8.0 %
8.0 %
ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
Shear Strength 0.004365 MPa

@Shear Rate 10.0 1/s,
Temperature 260 °C
 0.6330 psi

@Shear Rate 10.0 1/s,
Temperature 500 °F
 ISO 11403-1 -2
0.005825 MPa

@Shear Rate 10.0 1/s,
Temperature 250 °C
 0.8449 psi

@Shear Rate 10.0 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.007946 MPa

@Shear Rate 10.0 1/s,
Temperature 240 °C
 1.153 psi

@Shear Rate 10.0 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.1544 MPa

@Shear Rate 500 1/s,
Temperature 260 °C
 22.40 psi

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
0.1890 MPa

@Shear Rate 500 1/s,
Temperature 250 °C
 27.41 psi

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.2309 MPa

@Shear Rate 500 1/s,
Temperature 240 °C
 33.48 psi

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.5109 MPa

@Shear Rate 5000 1/s,
Temperature 260 °C
 74.10 psi

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
0.5653 MPa

@Shear Rate 5000 1/s,
Temperature 250 °C
 82.00 psi

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.6263 MPa

@Shear Rate 5000 1/s,
Temperature 240 °C
 90.83 psi

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Secant Modulus 0.43495 GPa

@Strain 7.01 %,
Temperature 40.0 °C
 63.085 ksi

@Strain 7.01 %,
Temperature 104 °F
 ISO 11403-1 -2
0.686 GPa

@Strain 3.64 %,
Temperature 40.0 °C
 99.5 ksi

@Strain 3.64 %,
Temperature 104 °F
 ISO 11403-1 -2
1.13 GPa

@Strain 1.27 %,
Temperature 40.0 °C
 164 ksi

@Strain 1.27 %,
Temperature 104 °F
 ISO 11403-1 -2
1.81 GPa

@Strain 5.21 %,
Temperature -40.0 °C
 262 ksi

@Strain 5.21 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.95 GPa

@Strain 3.80 %,
Temperature -20.0 °C
 282 ksi

@Strain 3.80 %,
Temperature -4.00 °F
 ISO 11403-1 -2
2.08 GPa

@Strain 2.17 %,
Temperature 23.0 °C
 302 ksi

@Strain 2.17 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.2825 GPa

@Strain 2.40 %,
Temperature 0.000 °C
 331.05 ksi

@Strain 2.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
2.37 GPa

@Strain 0.700 %,
Temperature 23.0 °C
 344 ksi

@Strain 0.700 %,
Temperature 73.4 °F
 ISO 11403-1 -2
2.4175 GPa

@Strain 3.20 %,
Temperature -40.0 °C
 350.63 ksi

@Strain 3.20 %,
Temperature -40.0 °F
 ISO 11403-1 -2
2.5695 GPa

@Strain 2.00 %,
Temperature -20.0 °C
 372.68 ksi

@Strain 2.00 %,
Temperature -4.00 °F
 ISO 11403-1 -2
2.62 GPa

@Strain 1.04 %,
Temperature 0.000 °C
 379 ksi

@Strain 1.04 %,
Temperature 32.0 °F
 ISO 11403-1 -2