DuPont Performance Polymers Crastin® 6129 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**)

Category Polymer , Thermoplastic , Polyester, TP , Polybutylene Terephthalate (PBT)
Manufacturer DuPont Performance Polymers
Trade Name Crastin®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Performance Polymers Crastin® 6129 NC010 Polybutylene Terephthalate (PBT)  (Unverified Data**).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Unreinforced High Viscosity Polybutylene Terephthalate Developed for Extrusion and Injection MoldingInformation provided by DuPont Performance Polymers
Physical Properties Metric English Comments
Density 1.12 g/cc
0.0405 lb/in³
1.32 g/cc
0.0477 lb/in³
ISO 1183
Water Absorption 0.40 %

@Thickness 2.00 mm
 0.40 %

@Thickness 0.0787 in
 Sim. to ISO 62
Moisture Absorption 0.200 %

@Thickness 2.00 mm
 0.200 %

@Thickness 0.0787 in
 Sim. to ISO 62
Viscosity 123300 cP

@Shear Rate 5000 1/s,
Temperature 260 °C
 123300 cP

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
142200 cP

@Shear Rate 5000 1/s,
Temperature 250 °C
 142200 cP

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
165000 cP

@Shear Rate 5000 1/s,
Temperature 240 °C
 165000 cP

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
396400 cP

@Shear Rate 500 1/s,
Temperature 260 °C
 396400 cP

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
505900 cP

@Shear Rate 500 1/s,
Temperature 250 °C
 505900 cP

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
626100 cP

@Shear Rate 10.0 1/s,
Temperature 260 °C
 626100 cP

@Shear Rate 10.0 1/s,
Temperature 500 °F
 ISO 11403-1 -2
641900 cP

@Shear Rate 500 1/s,
Temperature 240 °C
 641900 cP

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
918900 cP

@Shear Rate 10.0 1/s,
Temperature 250 °C
 918900 cP

@Shear Rate 10.0 1/s,
Temperature 482 °F
 ISO 11403-1 -2
1.3929e+6 cP

@Shear Rate 10.0 1/s,
Temperature 240 °C
 1.3929e+6 cP

@Shear Rate 10.0 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Viscosity Test 150 cm³/g
150 cm³/g
ISO 307 1157 1628
Linear Mold Shrinkage, Flow 0.017 cm/cm
0.017 in/in
ISO 294-4 2577
Linear Mold Shrinkage, Transverse 0.015 cm/cm
0.015 in/in
ISO 294-4 2577
Melt Flow 10 g/10 min

@Load 2.16 kg,
Temperature 250 °C
 10 g/10 min

@Load 4.76 lb,
Temperature 482 °F
 ISO 1133
Mechanical Properties Metric English Comments
Tensile Stress 0.410 MPa

@Strain 0.170 %,
Temperature 150 °C
 59.5 psi

@Strain 0.170 %,
Temperature 302 °F
 ISO 11403-1 -2
0.680 MPa

@Strain 0.170 %,
Temperature 90.0 °C
 98.6 psi

@Strain 0.170 %,
Temperature 194 °F
 ISO 11403-1 -2
4.10 MPa

@Strain 2.28 %,
Temperature 150 °C
 595 psi

@Strain 2.28 %,
Temperature 302 °F
 ISO 11403-1 -2
6.67 MPa

@Strain 4.80 %,
Temperature 150 °C
 967 psi

@Strain 4.80 %,
Temperature 302 °F
 ISO 11403-1 -2
7.25 MPa

@Strain 2.25 %,
Temperature 90.0 °C
 1050 psi

@Strain 2.25 %,
Temperature 194 °F
 ISO 11403-1 -2
8.25 MPa

@Strain 7.41 %,
Temperature 150 °C
 1200 psi

@Strain 7.41 %,
Temperature 302 °F
 ISO 11403-1 -2
12.07 MPa

@Strain 4.64 %,
Temperature 90.0 °C
 1751 psi

@Strain 4.64 %,
Temperature 194 °F
 ISO 11403-1 -2
13.63 MPa

@Strain 0.430 %,
Temperature -40.0 °C
 1977 psi

@Strain 0.430 %,
Temperature -40.0 °F
 ISO 11403-1 -2
14.34 MPa

@Strain 1.27 %,
Temperature 40.0 °C
 2080 psi

@Strain 1.27 %,
Temperature 104 °F
 ISO 11403-1 -2
15.07 MPa

@Strain 7.13 %,
Temperature 90.0 °C
 2186 psi

@Strain 7.13 %,
Temperature 194 °F
 ISO 11403-1 -2
16.61 MPa

@Strain 0.700 %,
Temperature 23.0 °C
 2409 psi

@Strain 0.700 %,
Temperature 73.4 °F
 ISO 11403-1 -2
22.95 MPa

@Strain 0.820 %,
Temperature -20.0 °C
 3329 psi

@Strain 0.820 %,
Temperature -4.00 °F
 ISO 11403-1 -2
24.96 MPa

@Strain 3.64 %,
Temperature 40.0 °C
 3620 psi

@Strain 3.64 %,
Temperature 104 °F
 ISO 11403-1 -2
27.2 MPa

@Strain 1.04 %,
Temperature 0.000 °C
 3950 psi

@Strain 1.04 %,
Temperature 32.0 °F
 ISO 11403-1 -2
29.39 MPa

@Strain 6.18 %,
Temperature 40.0 °C
 4263 psi

@Strain 6.18 %,
Temperature 104 °F
 ISO 11403-1 -2
32.22 MPa

@Strain 8.75 %,
Temperature 40.0 °C
 4673 psi

@Strain 8.75 %,
Temperature 104 °F
 ISO 11403-1 -2
45.2 MPa

@Strain 2.17 %,
Temperature 23.0 °C
 6560 psi

@Strain 2.17 %,
Temperature 73.4 °F
 ISO 11403-1 -2
48.4 MPa

@Strain 1.69 %,
Temperature -40.0 °C
 7020 psi

@Strain 1.69 %,
Temperature -40.0 °F
 ISO 11403-1 -2
51.39 MPa

@Strain 2.00 %,
Temperature -20.0 °C
 7454 psi

@Strain 2.00 %,
Temperature -4.00 °F
 ISO 11403-1 -2
54.78 MPa

@Strain 2.40 %,
Temperature 0.000 °C
 7945 psi

@Strain 2.40 %,
Temperature 32.0 °F
 ISO 11403-1 -2
65.05 MPa

@Strain 4.22 %,
Temperature 0.000 °C
 9435 psi

@Strain 4.22 %,
Temperature 32.0 °F
 ISO 11403-1 -2
70.55 MPa

@Strain 3.31 %,
Temperature -20.0 °C
 10230 psi

@Strain 3.31 %,
Temperature -4.00 °F
 ISO 11403-1 -2
71.25 MPa

@Strain 2.81 %,
Temperature -40.0 °C
 10330 psi

@Strain 2.81 %,
Temperature -40.0 °F
 ISO 11403-1 -2
77.04 MPa

@Strain 5.18 %,
Temperature -20.0 °C
 11170 psi

@Strain 5.18 %,
Temperature -4.00 °F
 ISO 11403-1 -2
87.67 MPa

@Strain 4.16 %,
Temperature -40.0 °C
 12720 psi

@Strain 4.16 %,
Temperature -40.0 °F
 ISO 11403-1 -2
95.86 MPa

@Strain 5.77 %,
Temperature -40.0 °C
 13900 psi

@Strain 5.77 %,
Temperature -40.0 °F
 ISO 11403-1 -2
Tensile Strength, Yield 58.0 MPa
8410 psi
ISO 527-1/-2
Elongation at Break >= 50 %
>= 50 %
Nominal; ISO 527-1/-2
Elongation at Yield 5.0 %
5.0 %
ISO 527-1/-2
Tensile Modulus 2.60 GPa
377 ksi
ISO 527-1/-2
0.251 GPa

@Temperature 120 °C
 36.4 ksi

@Temperature 248 °F
 ISO 11403-1 -2
1.162 GPa

@Temperature 40.0 °C
 168.5 ksi

@Temperature 104 °F
 ISO 11403-1 -2
3.024 GPa

@Temperature -40.0 °C
 438.6 ksi

@Temperature -40.0 °F
 ISO 11403-1 -2
Flexural Modulus 2.40 GPa
348 ksi
ISO 178
Shear Strength 0.006261 MPa

@Shear Rate 10.0 1/s,
Temperature 260 °C
 0.9081 psi

@Shear Rate 10.0 1/s,
Temperature 500 °F
 ISO 11403-1 -2
0.009189 MPa

@Shear Rate 10.0 1/s,
Temperature 250 °C
 1.333 psi

@Shear Rate 10.0 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.013929 MPa

@Shear Rate 10.0 1/s,
Temperature 240 °C
 2.0202 psi

@Shear Rate 10.0 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.1982 MPa

@Shear Rate 500 1/s,
Temperature 260 °C
 28.74 psi

@Shear Rate 500 1/s,
Temperature 500 °F
 ISO 11403-1 -2
0.2530 MPa

@Shear Rate 500 1/s,
Temperature 250 °C
 36.69 psi

@Shear Rate 500 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.3209 MPa

@Shear Rate 500 1/s,
Temperature 240 °C
 46.55 psi

@Shear Rate 500 1/s,
Temperature 464 °F
 ISO 11403-1 -2
0.6165 MPa

@Shear Rate 5000 1/s,
Temperature 260 °C
 89.42 psi

@Shear Rate 5000 1/s,
Temperature 500 °F
 ISO 11403-1 -2
0.7110 MPa

@Shear Rate 5000 1/s,
Temperature 250 °C
 103.1 psi

@Shear Rate 5000 1/s,
Temperature 482 °F
 ISO 11403-1 -2
0.8248 MPa

@Shear Rate 5000 1/s,
Temperature 240 °C
 119.6 psi

@Shear Rate 5000 1/s,
Temperature 464 °F
 ISO 11403-1 -2
Secant Modulus 0.43495 GPa

@Strain 7.01 %,
Temperature 40.0 °C
 63.085 ksi

@Strain 7.01 %,
Temperature 104 °F
 ISO 11403-1 -2
0.686 GPa

@Strain 3.64 %,
Temperature 40.0 °C
 99.5 ksi

@Strain 3.64 %,
Temperature 104 °F
 ISO 11403-1 -2
1.13 GPa

@Strain 1.27 %,
Temperature 40.0 °C
 164 ksi

@Strain 1.27 %,
Temperature 104 °F
 ISO 11403-1 -2
1.81 GPa

@Strain 5.21 %,
Temperature -40.0 °C
 262 ksi

@Strain 5.21 %,
Temperature -40.0 °F
 ISO 11403-1 -2
1.95 GPa

@Strain 3.80 %,
Temperature -20.0 °C
 282 ksi

@Strain 3.80 %,
Temperature -4.00 °F
 ISO 11403-1 -2