DuPont™ Dartek® F-101 Nylon 6,6 Forming Film, 25 µm Thickness  (discontinued **)

Category Polymer , Film , Thermoplastic , Nylon , Nylon 66 , Nylon 66, Film
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont™ Dartek® F-101 Nylon 6,6 Forming Film, 25 µm Thickness  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Data provided by DuPont Packaging Polymers.A cast nylon film made from type 6,6 polymer - the condensation product of adipic acid and hexamethylen diamine. It contains all the excellent properties historically found in Dartek®. Can be printed, laminated or extrusion coated. In converter combinations it may be used in any packaging end use which requires thermoforming, be it by vacuum, compressed air or mechanical means.
Physical Properties Metric English Comments
Density 1.13 g/cc
0.0408 lb/in³
Moisture Vapor Transmission 7.38 cc-mm/m²-24hr-atm

@Temperature 23.0 °C
18.7 cc-mil/100 in²-24hr-atm

@Temperature 73.4 °F
90% RH; ASTM E398-70
Water Vapor Transmission 295 g/m²/day

@Temperature 23.0 °C
19.0 g/100 in²/day

@Temperature 73.4 °F
90% RH; ASTM E398-70
Oxygen Transmission 1.40 cc-mm/m²-24hr-atm
3.56 cc-mil/100 in²-24hr-atm
or 54 cc/m²-24hr-atm for the film at 23°C, 0% RH. ASTM D1434-66
Mechanical Properties Metric English Comments
Film Elongation at Break, MD 300 %
300 %
ASTM D882-64T
Film Elongation at Break, TD 300 %
300 %
ASTM D882-64T
Secant Modulus, MD 0.690 GPa
100 ksi
ASTM D882
Secant Modulus, TD 0.690 GPa
100 ksi
ASTM D882
Coefficient of Friction, Dynamic 0.45
0.45
film to film; ASTM D1894-90
Elmendorf Tear Strength, MD 1.40 g/micron
35.6 g/mil
ASTM D1922-67
Elmendorf Tear Strength, TD 1.20 g/micron
30.5 g/mil
ASTM D1922-67
Dart Drop Test 600 g
1.32 lb
Impact Strength, ASTM D1709-62T
Film Tensile Strength at Break, MD 65.0 MPa
9430 psi
ASTM D882
Film Tensile Strength at Break, TD 65.0 MPa
9430 psi
ASTM D882
Optical Properties Metric English Comments
Haze 1.0 %
1.0 %
Gloss 150 %
150 %