DuPont Bexloy® AXW604BK 3% Glass Reinforced, Heat Stabilized Modified Ionomer Resin  (discontinued **)

Category Polymer , Thermoplastic , Ionomer , Ionomer, Molded
Manufacturer
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DuPont Bexloy® AXW604BK 3% Glass Reinforced, Heat Stabilized Modified Ionomer Resin  (discontinued **).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
A 3% glass reinforced, heat stabilized modified ionomer resin engineered for injection molded interior automotive applications.Availability: North AmericaInformation provided by DuPont.
Physical Properties Metric English Comments
Density 0.970 g/cc
0.0350 lb/in³
ASTM D792 - ISO 1183
Linear Mold Shrinkage, Flow 0.0075 cm/cm
0.0075 in/in
ASTM D955
Melt Flow 1.5 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.5 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238 - ISO 1133
Mechanical Properties Metric English Comments
Tensile Strength at Break 22.1 MPa
3200 psi
ASTM D638 - ISO 527-2
Elongation at Break 400 %
400 %
ASTM D638 - ISO 527-2
Flexural Modulus 0.7580 GPa
109.9 ksi
ASTM D790
Izod Impact, Notched 8.54 J/cm

@Temperature -30.0 °C
16.0 ft-lb/in

@Temperature -22.0 °F
ASTM D256
Gardner Impact 36.2 J

@Temperature -30.0 °C
26.7 ft-lb

@Temperature -22.0 °F
ASTM D3029
Impact Test 18.0 J

@Temperature -30.0 °C
13.2 ft-lb

@Temperature -22.0 °F
Rheometric, 5mph, 1/2" diameter tup, 3" diameter ring
21.9 J

@Temperature 22.8 °C
16.2 ft-lb

@Temperature 73.0 °F
Rheometric, 5mph, 1/2" diameter tup, 3" diameter ring
Thermal Properties Metric English Comments
CTE, linear 76.0 µm/m-°C

@Temperature -30.0 - 80.0 °C
42.2 µin/in-°F

@Temperature -22.0 - 176 °F
ASTM E831
Deflection Temperature at 0.46 MPa (66 psi) 80.0 °C
176 °F
ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 48.3 °C
119 °F
ASTM D648
Processing Properties Metric English Comments
Nozzle Temperature 238 - 271 °C
460 - 520 °F
Melt Temperature 238 - 288 °C
460 - 550 °F
Mold Temperature 15.6 - 60.0 °C
60.0 - 140 °F
Drying Temperature 60.0 - 79.4 °C
140 - 175 °F
Moisture Content <= 0.080 %
<= 0.080 %
Back Pressure >= 0.345 MPa
>= 50.0 psi
no units given
Descriptive Properties Value Comments
Heat Sag, 82°C 13 mm
ASTM D3773
Injection Speed Fast