- Dow Retain® 8209 ABS + Polycarbonate
Dow Retain® 8209 ABS + Polycarbonate
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Dow Chemical |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Retain® 8209 ABS + Polycarbonate.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Data provided by Dow Chemical.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.24 g/cc | 0.0448 lb/in³ | ASTM Data |
| Melt Density | 1.14 g/cc | 0.0412 lb/in³ | Melt density |
| Melt Flow | 22 g/10 min @Load 3.80 kg, Temperature 230 °C |
22 g/10 min @Load 8.38 lb, Temperature 446 °F |
ASTM Data |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 121 | 121 | |
| Tensile Strength, Ultimate | 86.0 MPa | 12500 psi | ASTM Data |
| Elongation at Break | 3.0 % | 3.0 % | ASTM Data |
| Tensile Modulus | 4.74 GPa | 687 ksi | ASTM Data |
| Izod Impact, Notched | 0.960 J/cm | 1.80 ft-lb/in | ASTM Data |
| 0.910 J/cm @Temperature -50.0 °C |
1.70 ft-lb/in @Temperature -58.0 °F |
ASTM Data | |
| Izod Impact, Unnotched | 5.39 J/cm | 10.1 ft-lb/in | ASTM Data |
| Impact Test | 4.00 J @Temperature -30.0 °C |
2.95 ft-lb @Temperature -22.0 °F |
Instrumented Dart Total Energy |
| 5.00 J @Temperature 23.0 °C |
3.69 ft-lb @Temperature 73.4 °F |
Instrumented Dart Total Energy |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Heat Capacity | 1.99 J/g-°C | 0.476 BTU/lb-°F | |
| Thermal Conductivity | 0.221 W/m-K | 1.53 BTU-in/hr-ft²-°F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 133 °C | 271 °F | Unannealed; ASTM Data |
| Deflection Temperature at 1.8 MPa (264 psi) | 125 °C | 257 °F | Unannealed; ASTM Data |
| Vicat Softening Point | 139 °C | 282 °F |