Dow Questra® WA206 High Heat Syndiotactic Polystyrene, 40% Glass Filled (discontinued **)

Category	Polymer , Thermoplastic , Polystyrene (PS) , Syndiotactic Polystyrene (SPS) , Syndiotactic Polystyrene (SPS) with Glass or Carbon Fiber
Manufacturer
Trade Name
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow Questra® WA206 High Heat Syndiotactic Polystyrene, 40% Glass Filled (discontinued **).pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

QUESTRA® Crystalline Polymers are semi-crystalline engineering thermoplastic resins produced from styrene monomer using a proprietary metallocene catalyst system. These syndiotactic polymers are very different from conventional styrenics in structure, and properties, exhibiting excellent heat resistance with a melting temperature of 270.C, 0excellent moisture and chemical resistance together with a unique combination of exceptional electrical properties, toughness and processability. QUESTRA crystalline polymers are typically used as moldings, films, and fibers in Electronic, Electrical, Automotive, Consumer and Industrial, Filtration, Optical/photographic film and Specialty fiber/non-woven markets. QUESTRA WA206 is a 40% glass filled polymer suitable for Automotive Systems.Data provided by Dow Chemical.

Physical Properties	Metric	English	Comments
Density	1.32 g/cc	0.0477 lb/in³	ASTM Data
Water Absorption	0.010 %	0.010 %

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	132 MPa	19100 psi	ASTM Data
Tensile Strength, Yield	132 MPa	19100 psi	ASTM Data
Tensile Modulus	11.2 GPa	1620 ksi	ASTM Data
Izod Impact, Notched	1.12 J/cm	2.10 ft-lb/in	ASTM Data

Thermal Properties	Metric	English	Comments
CTE, linear, Parallel to Flow	17.1 µm/m-°C @Temperature 20.0 °C	9.50 µin/in-°F @Temperature 68.0 °F	ASTM data
Deflection Temperature at 0.46 MPa (66 psi)	263 °C	505 °F	Unannealed; ASTM Data
Deflection Temperature at 1.8 MPa (264 psi)	249 °C	480 °F	Unannealed; ASTM Data
Vicat Softening Point	263 °C	505 °F