Dow INTEGRAL™ 917 Monolayer Bonding Film

Category Polymer , Film , Thermoset
Manufacturer Dow Chemical
Trade Name INTEGRAL™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow INTEGRAL™ 917 Monolayer Bonding Film.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
INTEGRAL 917 Adhesive Film is a single layer adhesive film for use where a higher flow rate and lower melt point are required. It is useful for bonding heat sensitive materials, or for porous substrates, and can be used to bond fabric to foam, paper to foil, or olefin sheet to non-woven textiles.Information provided by Dow
Physical Properties Metric English Comments
Thickness 50.8 microns
2.00 mil
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 10.3 MPa
1500 psi
ASTM D882
Film Tensile Strength at Yield, TD 8.27 MPa
1200 psi
ASTM D882
Film Elongation at Break, MD 200 %
200 %
ASTM D882
Film Elongation at Break, TD 400 %
400 %
ASTM D882
Secant Modulus, MD 0.131 GPa
19.0 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.138 GPa
20.0 ksi
2% Secant; ASTM D882
Elmendorf Tear Strength, MD 5.51 g/micron
140 g/mil
ASTM D882
Elmendorf Tear Strength, TD 3.74 g/micron
95.0 g/mil
ASTM D882
Film Tensile Strength at Break, MD 25.5 MPa
3700 psi
ASTM D882
Film Tensile Strength at Break, TD 16.5 MPa
2400 psi
ASTM D882