Dow INSPIRE™ D118.01 Developmental Performance Polymer

Category	Polymer , Thermoplastic , Polypropylene (PP)
Manufacturer	Dow Chemical
Trade Name	INSPIRE™
Port	Shanghai port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow INSPIRE™ D118.01 Developmental Performance Polymer.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

D118.01 Developmental Performance Polymer is a propylene-based resin intended for use in film and sheet extrusion. Film and sheet produced from this resin offer improved stiffness, heat resistance, machinablility, and toughness over competitive cast polypropylene films. Coextruded structures offer a broad range of potentially improved properties including high stiffness, good clarity and barrier properties. It has high film stiffness/ machinability, high heat resistance, excellent processability, and it complies with U.S. FDA 21 CFR 177.1520(c) 1.1aInformation provided by Dow

Physical Properties	Metric	English	Comments
Density	0.900 g/cc	0.0325 lb/in³	ASTM D792
Melt Flow	8.0 g/10 min @Load 2.16 kg, Temperature 230 °C	8.0 g/10 min @Load 4.76 lb, Temperature 446 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Film Tensile Strength at Yield, MD	31.46 MPa	4563 psi	ASTM D882
Film Tensile Strength at Yield, TD	30.40 MPa	4409 psi	ASTM D882
Film Elongation at Break, MD	527 %	527 %	ASTM D882
Film Elongation at Break, TD	6.0 %	6.0 %	ASTM D882
Tensile Modulus	1.06 GPa	154 ksi	CD, 2% Secant; ASTM D882
	1.07 GPa	155 ksi	MD, 2% Secant; ASTM D882
Film Tensile Strength at Break, MD	55.49 MPa	8048 psi	ASTM D882
Film Tensile Strength at Break, TD	30.40 MPa	4409 psi	ASTM D882