Dow HDPE 05862N High Density Polyethylene

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , HDPE , High Density Polyethylene (HDPE), Injection Molded
Manufacturer Dow Chemical
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow HDPE 05862N High Density Polyethylene.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Film properties below based on a film thickness of 25 µm. Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 0.963 g/cc
0.0348 lb/in³
Thickness 25.0 microns
0.984 mil
Melt Flow 5.0 g/10 min

@Load 2.16 kg
5.0 g/10 min

@Load 4.76 lb
Melt flow ratio I10/I2 is 8.1.
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 27.5 MPa
3990 psi
Film Tensile Strength at Yield, TD 28.3 MPa
4100 psi
Film Elongation at Break, MD 595 %
595 %
Film Elongation at Break, TD 650 %
650 %
Secant Modulus, MD 0.472 GPa
68.5 ksi
Film value
Secant Modulus, TD 0.572 GPa
83.0 ksi
Film value
Elmendorf Tear Strength MD 40 g
40 g
Elmendorf Tear Strength TD 118 g
118 g
Elmendorf Tear Strength, MD 1.60 g/micron
40.6 g/mil
Elmendorf Tear Strength, TD 4.70 g/micron
119 g/mil
Dart Drop 1.60 g/micron
40.6 g/mil
Film Tensile Strength at Break, MD 35.6 MPa
5160 psi
Film Tensile Strength at Break, TD 28.0 MPa
4060 psi
Thermal Properties Metric English Comments
Vicat Softening Point 130 °C
266 °F
Optical Properties Metric English Comments
Haze 6.0 %
6.0 %
Gloss 85 %
85 %
45°
Processing Properties Metric English Comments
Processing Temperature 274 °C
525 °F
Film extrusion temperature