Dow FLEXOMER™ GERS-1088 NT Very Low Density Polyethylene (VLDPE) Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Dow Chemical
Trade Name FLEXOMER™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow FLEXOMER™ GERS-1088 NT Very Low Density Polyethylene (VLDPE) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FLEXOMER™ GERS-1088 NT is an ethylene-butene copolymer produced via gas phase polymerization from Dow. It can be utilized in monolayer and co-extruded films and in blends with other polyolefins to enhance melt strength and toughness of the structure. Granular form enhances rapid melt blending into polypropylene or polyethylene. Information provided by Dow
Physical Properties Metric English Comments
Density 0.884 g/cc
0.0319 lb/in³
ASTM D792
High Load Melt Index 5.0 g/10 min

@Load 21.6 kg,
Temperature 190 °C
5.0 g/10 min

@Load 47.6 lb,
Temperature 374 °F
ASTM D1238
Melt Index of Compound 0.090 g/10 min

@Load 2.16 kg,
Temperature 190 °C
0.090 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 81
81
1 sec; molded and tested in accordance with ASTM D4976; ASTM D2240
82
82
5 sec; molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break 8.27 MPa
1200 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break 500 %
500 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus 0.0310 GPa
4.50 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 A
Thermal Properties Metric English Comments
Melting Point 115 °C
239 °F
Dow Method (DSC)
Glass Transition Temp, Tg -47.8 °C
-54.0 °F
Dow Method