Dow FLEXOMER™ ETS-9064 NT 7, 0.8 mil Very Low Density Polyethylene (VLDPE) Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LDPE
Manufacturer Dow Chemical
Trade Name FLEXOMER™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow FLEXOMER™ ETS-9064 NT 7, 0.8 mil Very Low Density Polyethylene (VLDPE) Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
FLEXOMER™ ETS-9064 NT 7 is intended for use in single of multi-layer blown-film constructions or thick sheets. Films extruded from ETS-9064 NT 7 have a high tear strength, high impact strength, and high puncture resistance and are readily heat sealable.Information provided by Dow
Physical Properties Metric English Comments
Density 0.911 g/cc
0.0329 lb/in³
ASTM D792
Thickness 20.3 microns
0.800 mil
Melt Flow 1.0 g/10 min
1.0 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 9.65 MPa
1400 psi
ASTM D882
Film Tensile Strength at Yield, TD 9.65 MPa
1400 psi
ASTM D882
Film Elongation at Break, MD 570 %
570 %
ASTM D882
Film Elongation at Break, TD 930 %
930 %
ASTM D882
Secant Modulus, MD 0.1613 GPa
23.40 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.17099 GPa
24.800 ksi
2% Secant; ASTM D882
Impact 325
325
[ft-lbf/in<sup>3</sup>]; Puncture Resistance; Dow Method
2700
2700
[ft-lbf/in<sup>3</sup>]; Toughness MD; ASTM D882
4200
4200
[ft-lbf/in<sup>3</sup>]; Toughness TD; ASTM D882
Elmendorf Tear Strength MD 400 g
400 g
ASTM D1922
Elmendorf Tear Strength TD 500 g
500 g
ASTM D1922
Elmendorf Tear Strength, MD 19.7 g/micron
500 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 24.6 g/micron
625 g/mil
ASTM D1922
Dart Drop Test 170 g
0.375 lb
Method B; ASTM D1709
Film Tensile Strength at Break, MD 51.7 MPa
7500 psi
ASTM D882
Film Tensile Strength at Break, TD 49.6 MPa
7200 psi
ASTM D882
Heat Seal Strength Initiation Temperature 90.0 °C
194 °F
1 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 122 °C
252 °F
Dow Method (DSC)
Vicat Softening Point 94.0 °C
201 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 9.8 %
9.8 %
ASTM D1003
Gloss 58 %
58 %
45°; ASTM D2457
Transmission, Visible 98 %
98 %
Clarity; ASTM D1746