Dow ELITE™ 5110G Enhanced Polyethylene Resin

Category Polymer , Film , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name ELITE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow ELITE™ 5110G Enhanced Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
ELITE™ 5110G is a copolymer produced via INSITE™ Technology from Dow Plastics. It offers a unique combination of high modulus and excellent impact strength, allowing for down gauging in bag applications. ELLITE™ 5110G resin complies with U.S. FDA regulation 21 CFR 177.1520 (c) 3.2a when used unmodified and processed according to good manufacturing practices.Information provided by Dow
Physical Properties Metric English Comments
Density 0.9255 g/cc
0.03344 lb/in³
ASTM D792
Thickness 50.8 microns
2.00 mil
Melt Flow 0.85 g/10 min
0.85 g/10 min
ASTM D1238
Mechanical Properties Metric English Comments
Film Tensile Strength at Yield, MD 13.89 MPa
2015 psi
ASTM D882
Film Tensile Strength at Yield, TD 14.58 MPa
2115 psi
ASTM D882
Film Elongation at Break, MD 597 %
597 %
ASTM D882
Film Elongation at Break, TD 660 %
660 %
ASTM D882
Secant Modulus, MD 0.2769 GPa
40.16 ksi
2% Secant; ASTM D882
Secant Modulus, TD 0.3303 GPa
47.91 ksi
2% Secant; ASTM D882
Impact 21.8
21.8
[lb<sub>f</sub>]; Puncture Resistance Force; Dow Method
Puncture Energy 6.91 J
5.10 ft-lb
Dow Method
Elmendorf Tear Strength MD 564 g
564 g
ASTM D1922
Elmendorf Tear Strength TD 1110 g
1110 g
ASTM D1922
Elmendorf Tear Strength, MD 11.1 g/micron
282 g/mil
ASTM D1922
Elmendorf Tear Strength, TD 21.9 g/micron
555 g/mil
ASTM D1922
Dart Drop Test 409 g
0.902 lb
Method B; ASTM D1709
Film Tensile Strength at Break, MD 57.50 MPa
8339 psi
ASTM D882
Film Tensile Strength at Break, TD 51.95 MPa
7534 psi
ASTM D882
Heat Seal Strength Initiation Temperature 120 °C
248 °F
2 lb/in heat seal strength; 0.5 sec dwell, 40 psi bar pressure, pull speed 10 (in./min.); Dow Method
Thermal Properties Metric English Comments
Melting Point 123 °C
253 °F
Dow Method (DSC)
Vicat Softening Point 111 °C
232 °F
ASTM D1525
Optical Properties Metric English Comments
Haze 13 %
13 %
ASTM D1003
Gloss 60 %
60 %
45°; ASTM D2457