Dow DOWLEX™ 2535 Linear Low Density Polyethylene, Narrow MW Distribution

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer Dow Chemical
Trade Name DOWLEX™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DOWLEX™ 2535 Linear Low Density Polyethylene, Narrow MW Distribution.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOWLEX® 2535 Polyethylene resin is a narrow molecular weight distribution copolymer designed to offer excellent impact strength and stress crack resistance with good flexibility. It has good processability over a wide range of molding conditions. This material complies with U.S. FDA Regulation 21 CFR 177.1520 (c) 3.1 (a) for food packaging applications. The regulation should be consulted for complete details.Data provided by Dow Chemical.
Physical Properties Metric English Comments
Density 0.919 g/cc
0.0332 lb/in³
Viscosity 82000 cP

@Shear Rate 5000 1/s,
Temperature 190 °C
82000 cP

@Shear Rate 5000 1/s,
Temperature 374 °F
Apparent Dynamic Viscosity
180000 cP

@Shear Rate 1000 1/s,
Temperature 190 °C
180000 cP

@Shear Rate 1000 1/s,
Temperature 374 °F
Apparent Dynamic Viscosity
300000 cP

@Shear Rate 300 1/s,
Temperature 190 °C
300000 cP

@Shear Rate 300 1/s,
Temperature 374 °F
Apparent Dynamic Viscosity
Melt Flow 6.0 g/10 min

@Load 2.16 kg
6.0 g/10 min

@Load 4.76 lb
Melt flow ratio I10/I2 is 7.5.
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 12.7 MPa
1840 psi
Tensile Strength, Yield 8.10 MPa
1170 psi
Elongation at Break 560 %
560 %
Modulus of Elasticity 0.174 GPa
25.2 ksi
Molded Sample 2% Secant Modulus
Flexural Modulus 0.327 GPa
47.4 ksi
Izod Impact, Notched (ISO) 97.0 kJ/m²

@Temperature -50.0 °C
46.2 ft-lb/in²

@Temperature -58.0 °F
Thermal Properties Metric English Comments
Vicat Softening Point 94.0 °C
201 °F