Dow DOWLEX™ 2517 Linear Low Density Polyethylene, Narrow MW Distribution

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer	Dow Chemical
Trade Name	DOWLEX™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow DOWLEX™ 2517 Linear Low Density Polyethylene, Narrow MW Distribution.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DOWLEX® 2517 Polyethylene resin is a narrow molecular weight distribution copolymer designed to offer excellent environmental stress crack resistance and low temperature properties with excellent flexibility. It has good processability over a wide range of molding conditions. It complies with U.S. FDA Regulation 21 CFR 177.1520 (c) 3.1 (b) for food packaging applications. The regulation should be consulted for complete details.Data provided by Dow Chemical.

Physical Properties	Metric	English	Comments
Density	0.917 g/cc	0.0331 lb/in³
Viscosity	47000 cP @Shear Rate 5000 1/s, Temperature 190 °C	47000 cP @Shear Rate 5000 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
	86000 cP @Shear Rate 1000 1/s, Temperature 190 °C	86000 cP @Shear Rate 1000 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
	110000 cP @Shear Rate 300 1/s, Temperature 190 °C	110000 cP @Shear Rate 300 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
Melt Flow	25 g/10 min @Load 2.16 kg	25 g/10 min @Load 4.76 lb	Melt flow ratio I10/I2 is 7.3.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	11.1 MPa	1610 psi
Tensile Strength, Yield	7.30 MPa	1060 psi
Elongation at Break	650 %	650 %
Modulus of Elasticity	0.150 GPa	21.8 ksi	Molded Sample 2% Secant Modulus
Flexural Modulus	0.317 GPa	46.0 ksi
Izod Impact, Notched (ISO)	61.0 kJ/m² @Temperature -50.0 °C	29.0 ft-lb/in² @Temperature -58.0 °F

Thermal Properties	Metric	English	Comments
Vicat Softening Point	88.0 °C	190 °F