Dow DOWLEX™ 2503 Linear Low Density Polyethylene, Narrow MW Distribution

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer	Dow Chemical
Trade Name	DOWLEX™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow DOWLEX™ 2503 Linear Low Density Polyethylene, Narrow MW Distribution.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DOWLEX® 2503 Polyethylene resin is a narrow molecular weight distribution copolymer designed to offer excellent environmental stress crack resistance and tear strength with excellent rigidity. It has excellent processability over a wide range of molding conditions. This material complies with U.S. FDA Regulation 21 CFR 177.1520 c 3.1(a) for food packaging applications. The regulation should be consulted for complete details.Data provided by Dow Chemical.

Physical Properties	Metric	English	Comments
Density	0.930 g/cc	0.0336 lb/in³
Viscosity	21000 cP @Shear Rate 5000 1/s, Temperature 190 °C	21000 cP @Shear Rate 5000 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
	29000 cP @Shear Rate 1000 1/s, Temperature 190 °C	29000 cP @Shear Rate 1000 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
	31000 cP @Shear Rate 300 1/s, Temperature 190 °C	31000 cP @Shear Rate 300 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
Melt Flow	105 g/10 min @Load 2.16 kg	105 g/10 min @Load 4.76 lb	Melt flow ratio I10/I2 is 6.5.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	8.20 MPa	1190 psi
Tensile Strength, Yield	10.6 MPa	1540 psi
Elongation at Break	450 %	450 %
Modulus of Elasticity	0.273 GPa	39.6 ksi	Molded Sample 2% Secant Modulus
Flexural Modulus	0.503 GPa	73.0 ksi
Izod Impact, Notched (ISO)	23.0 kJ/m² @Temperature -50.0 °C	10.9 ft-lb/in² @Temperature -58.0 °F

Thermal Properties	Metric	English	Comments
Vicat Softening Point	100 °C	212 °F

Users viewing this material also viewed the following: