Dow DOWLEX™ 2500 Linear Low Density Polyethylene, Narrow MW Distribution

Category	Polymer , Thermoplastic , Polyethylene (PE) , LLDPE , Linear Low Density Polyethylene (LLDPE), Injection Molded
Manufacturer	Dow Chemical
Trade Name	DOWLEX™
Port	Ningbo port,China
Trade Terms	FOB, CFR, CIF
Payment Terms	L/C, T/T, Western Union
Download PDF	Dow DOWLEX™ 2500 Linear Low Density Polyethylene, Narrow MW Distribution.pdf
Price	EMAIL US sales@lookpolymers.com
	Online Service lookpolymers 27660005

Material Notes:

DOWLEX® 2500 Polyethylene resin is a narrow molecular weight distribution copolymer designed to offer excellent environmental stress crack resistance and tear strength with high impact strength. It provides good processability over a wide range of molding conditions. This material complies with U.S. FDA Regulation 21 CFR 177.1520 c 3.1(a) for food packaging applications. The regulation should be consulted for complete details.Data provided by Dow Chemical.

Physical Properties	Metric	English	Comments
Density	0.925 g/cc	0.0334 lb/in³
Viscosity	35000 cP @Shear Rate 5000 1/s, Temperature 190 °C	35000 cP @Shear Rate 5000 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
	60000 cP @Shear Rate 1000 1/s, Temperature 190 °C	60000 cP @Shear Rate 1000 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
	73000 cP @Shear Rate 300 1/s, Temperature 190 °C	73000 cP @Shear Rate 300 1/s, Temperature 374 °F	Apparent Dynamic Viscosity
Melt Flow	58 g/10 min @Load 2.16 kg	58 g/10 min @Load 4.76 lb	Melt flow ratio I10/I2 is 6.8.

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	9.40 MPa	1360 psi
Tensile Strength, Yield	10.8 MPa	1570 psi
Elongation at Break	910 %	910 %
Modulus of Elasticity	0.210 GPa	30.5 ksi	Molded Sample 2% Secant Modulus
Flexural Modulus	0.380 GPa	55.1 ksi
Izod Impact, Notched (ISO)	45.0 kJ/m² @Temperature -50.0 °C	21.4 ft-lb/in² @Temperature -58.0 °F

Thermal Properties	Metric	English	Comments
Vicat Softening Point	97.2 °C	207 °F