Dow DNDA-9810 NT 7 Linear Low Density Polyethylene Resin

Category Polymer , Thermoplastic , Polyethylene (PE) , LLDPE
Manufacturer Dow Chemical
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow DNDA-9810 NT 7 Linear Low Density Polyethylene Resin.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
DOW DNDA-9810 NT 7 is produced using UNIPOL™ PE process technology and is supplied in pellet form. This resin is specifically designed as a carrier resin for color concentrates and other masterbatch systems. Information provided by Dow
Physical Properties Metric English Comments
Density 0.929 g/cc
0.0336 lb/in³
ASTM D792
ESCR 100% Igepal® <= 1.0 hour

@Temperature 50.0 °C
<= 1.0 hour

@Temperature 122 °F
F<sub>50</sub>; Molded and tested in accordance with ASTM D4976; ASTM D1693
Melt Index of Compound 100 g/10 min

@Load 2.16 kg,
Temperature 190 °C
100 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore D 53
53
Molded and tested in accordance with ASTM D4976; ASTM D2240
Tensile Strength at Break 8.27 MPa
1200 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Tensile Strength, Yield 11.0 MPa
1600 psi
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Break 120 %
120 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Elongation at Yield 2.0 %
2.0 %
Molded and tested in accordance with ASTM D4976; ASTM D638
Flexural Modulus 0.524 GPa
76.0 ksi
2% Secant; Molded and tested in accordance with ASTM D4976; ASTM D790 B
Tensile Impact Strength 168 kJ/m²
80.0 ft-lb/in²
Molded and tested in accordance with ASTM D4976; ASTM D1822, Type S
Thermal Properties Metric English Comments
Melting Point 126 °C
259 °F
Dow Method (DSC)
Crystallization Temperature 112 °C
234 °F
Dow Method (DSC)
Deflection Temperature at 0.46 MPa (66 psi) 47.2 °C
117 °F
Molded and tested in accordance with ASTM D4976; ASTM D648
Vicat Softening Point 96.1 °C
205 °F
ASTM D1525
Brittleness Temperature -30.0 °C
-22.0 °F
Molded and tested in accordance with ASTM D4976; ASTM D746