Dow Corning SILASTIC® 94-599-HC SILICONE RUBBER PART A&B
| Category | Polymer , Thermoset , Rubber or Thermoset Elastomer (TSE) , Silicone , Silicone Rubber |
| Manufacturer | Dow Corning |
| Trade Name | SILASTIC® |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Dow Corning SILASTIC® 94-599-HC SILICONE RUBBER PART A&B.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
47 Durometer, 2-part, 1 to 1 mix, translucent, molding grade, Liquid Silicone Rubber.Information provided by Dow Corning
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.15 g/cc @Temperature 25.0 °C |
1.15 g/cc @Temperature 77.0 °F |
|
| Solids Content | 100 % | 100 % |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 49 | 49 | |
| Tensile Strength, Ultimate | 11.0 MPa | 1590 psi | |
| Tensile Strength, Yield | 1.38 MPa | 200 psi | at 150% elongation, maximum |
| Elongation at Break | 590 % | 590 % | |
| Tear Strength | 32.4 kN/m | 185 pli | |
| Compression Set | 23 % | 23 % |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 5.50e+14 ohm-cm | 5.50e+14 ohm-cm | |
| Dielectric Constant | 2.89 @Frequency 100000 Hz |
2.89 @Frequency 100000 Hz |
|
| 2.91 @Frequency 100 Hz |
2.91 @Frequency 100 Hz |
||
| Dielectric Strength | 18.1 kV/mm | 460 kV/in | |
| Dissipation Factor | 0.0022 @Frequency 100000 Hz |
0.0022 @Frequency 100000 Hz |
|
| 0.0047 @Frequency 100 Hz |
0.0047 @Frequency 100 Hz |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Pot Life | 1440 min | 1440 min | |
| Shelf Life | 18.0 Month | 18.0 Month |
| Descriptive Properties | Value | Comments |
|---|---|---|
| Appearance | clear | |
| Mix Ratio (X:1) | 100 | Base to Catalyst ETN |