Dow BETAMATE™ XW 1185 Epoxy

Category Polymer , Thermoset , Epoxy
Manufacturer Dow Chemical
Trade Name BETAMATE™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow BETAMATE™ XW 1185 Epoxy.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
BETAMATE™ XW 1185 is a one component heat curing Epoxy paste adhesive. The material is readily pumped at ambient temperatures. It shows excellent adhesion to automotive steel and aluminum, is resistant to degradation and to substrate corrosion on environmental aging. The product is compatible with electro-coat paint process.Information provided by Dow
Physical Properties Metric English Comments
Density 1.28 - 1.34 g/cc
0.0462 - 0.0484 lb/in³
Solids Content >= 99 %
>= 99 %
Viscosity 350000 cP

@Shear Rate 1.00 1/s,
Temperature 23.0 °C
350000 cP

@Shear Rate 1.00 1/s,
Temperature 73.4 °F
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 13.0 MPa
1890 psi
ISO 527-1
Elongation at Break 11 %
11 %
ISO 527-1
Modulus of Elasticity 0.560 GPa
81.2 ksi
ISO 527-1
Adhesive Bond Strength 13.8 MPa

@Thickness 1.50 mm
2000 psi

@Thickness 0.0591 in
Lap Shear (CRS St 1203); EN 1465
15.9 MPa

@Thickness 0.750 mm
2310 psi

@Thickness 0.0295 in
Lap Shear (CRS St 1203); EN 1465
Peel Strength 3.30 kN/m
18.8 pli
T-Peel (CRS St 1203, 0.5mm)
8.00 kN/m
45.6 pli
Impact Peel
Thermal Properties Metric English Comments
Flash Point >= 100 °C
>= 212 °F
Processing Properties Metric English Comments
Cure Time 30.0 min

@Temperature 180 °C
0.500 hour

@Temperature 356 °F