Dow AMPLIFY™ EA 103 Ethylene-ethyl Acrylate (EEA)

Category Polymer , Thermoplastic
Manufacturer Dow Chemical
Trade Name AMPLIFY™
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow AMPLIFY™ EA 103 Ethylene-ethyl Acrylate (EEA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMPLIFY™ EA 103 Functional Polymer is produced via a high pressure reactor. It exhibits high flexibility and imparts low temperature toughness to a wide range of engineering resins. It can be utilized as in a hot metal adhesive formulation due to the high thermal stability it offers. It is an excellent base component for a film laminate and has marginal RF welding capability. This polymer demonstrates excellent blend compatibility with other polyolefins. It can be utilized as a tie layer between polyolefins and a variety of polar substrates, such as metal, polyvinylidiene chloride (PVDC), polyolefins, cellulose, polyester, polycarbonate, glass, foil, PVC, PET, and Polystyrene.Information provided by Dow
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
ASTM D792
Filler Content 19.5 %
19.5 %
Comonomer; ASTM D4094
Melt Flow 21 g/10 min

@Load 2.16 kg,
Temperature 190 °C
21 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 82
82
ASTM D2240
Hardness, Shore D 27
27
ASTM D2240
Tensile Strength, Ultimate 9.65 MPa
1400 psi
ASTM D638
Tensile Strength, Yield 2.59 MPa
375 psi
ASTM D638
Elongation at Break 750 %
750 %
ASTM D638
Elongation at Yield 11 %
11 %
ASTM D638
Flexural Modulus 0.0427 GPa
6.20 ksi
2% Secant; ASTM D790
Tensile Impact Strength 504 kJ/m²
240 ft-lb/in²
ASTM D1822, Type S
Thermal Properties Metric English Comments
Melting Point 95.0 °C
203 °F
Dow Method
Crystallization Temperature 78.0 °C
172 °F
Dow Method
Deflection Temperature at 0.46 MPa (66 psi) 31.1 °C
88.0 °F
ASTM D648
Vicat Softening Point 48.9 °C
120 °F
ASTM D1525
Brittleness Temperature <= -83.0 °C
<= -117 °F
ASTM D746