Dow AMPLIFY™ EA 100 Ethylene-ethyl Acrylate (EEA)

Category Polymer , Thermoplastic
Manufacturer Dow Chemical
Trade Name AMPLIFY™
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Dow AMPLIFY™ EA 100 Ethylene-ethyl Acrylate (EEA).pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
AMPLIFY™ EA 100 Functional Polymer is produced via a high pressure reactor. It exhibits high flexibility and imparts low temperature toughness to a wide range of engineering resins. This polymer demonstrates excellent blend compatibility with other polyolefins. It can be utilized as a tie layer between polyolefins and a variety of polar substrates, such as metal, polyvinylidiene chloride (PVDC), polyolefins, cellulose, polyester, polycarbonate, glass, foil, PVC, PET, and Polystyrene.Information provided by Dow
Physical Properties Metric English Comments
Density 0.930 g/cc
0.0336 lb/in³
ASTM D792
Filler Content 15 %
15 %
Comonomer; ASTM D4094
Melt Flow 1.3 g/10 min

@Load 2.16 kg,
Temperature 190 °C
1.3 g/10 min

@Load 4.76 lb,
Temperature 374 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Shore A 87
87
ASTM D2240
Hardness, Shore D 37
37
ASTM D2240
Tensile Strength, Ultimate 17.9 MPa
2600 psi
ASTM D638
Tensile Strength, Yield 3.79 MPa
550 psi
ASTM D638
Elongation at Break 750 %
750 %
ASTM D638
Elongation at Yield 8.0 %
8.0 %
ASTM D638
Flexural Modulus 0.0669 GPa
9.70 ksi
2% Secant; ASTM D790
Tensile Impact Strength NB
NB
ASTM D1822, Type S
Thermal Properties Metric English Comments
Melting Point 99.0 °C
210 °F
Dow Method
Crystallization Temperature 82.0 °C
180 °F
Dow Method
Deflection Temperature at 0.46 MPa (66 psi) 32.8 °C
91.0 °F
ASTM D648
Vicat Softening Point 67.2 °C
153 °F
ASTM D1525
Brittleness Temperature <= -76.0 °C
<= -105 °F
ASTM D746