Songhan Plastic Technology Co.,Ltd.
 POLYMER SEARCH

Diamond Polymers TR 5000

Category Polymer , Thermoplastic , ABS Polymer , Acrylonitrile Butadiene Styrene (ABS), Transparent, Molded
Manufacturer Diamond and Network Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers TR 5000.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Description: Transparent ABSInformation provided by Diamond Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.11 g/cc
1.11 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0070 cm/cm
0.0040 - 0.0070 in/in
ASTM D955
Melt Flow 2.1 g/10 min

@Load 5.00 kg,
Temperature 200 °C
2.1 g/10 min

@Load 11.0 lb,
Temperature 392 °F
Procedure A Condition G; ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 112
112
ASTM D785
Tensile Strength, Yield 48.85 MPa
7085 psi
chs 2 in/min; ASTM D638
Flexural Modulus 2.30 GPa
334 ksi
Procedure B, Test Method I(chs 0.05 in/min); ASTM D790
Izod Impact, Notched 1.07 J/cm
2.00 ft-lb/in
Test Method A (0.125 in bar); ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 72.8 °C
163 °F
0.125 in bar Unannealed/Conditioned 48 hours at 23°C; ASTM D648
Optical Properties Metric English Comments
Haze 4.2 %

@Thickness 3.00 mm
4.2 %

@Thickness 0.118 in
ASTM D1003
Transmission, Visible 88 %

@Thickness 3.00 mm
88 %

@Thickness 0.118 in
ASTM D1003
Processing Properties Metric English Comments
Middle Barrel Temperature 190 - 250 °C
374 - 482 °F
Mold Temperature 40.0 - 60.0 °C
104 - 140 °F
Higher mold temperature provides a product with excellent surface finishing and less residual stress.
Drying Temperature 80.0 - 85.0 °C
176 - 185 °F
Dry Time 2 - 4 hour
2 - 4 hour
Injection Pressure 4.83 - 7.58 MPa
700 - 1100 psi