Diamond Polymers SBS 1001 Styrene Butadiene Block Copolymer
| Category | Polymer , Thermoplastic , Styrene-Butadiene , Styrene-Butadiene Copolymer, SBC |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers SBS 1001 Styrene Butadiene Block Copolymer.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.02 g/cc | 1.02 g/cc | ASTM D792 |
| Water Absorption | 0.070 % @Temperature 23.0 °C |
0.070 % @Temperature 73.4 °F |
Saturation; ASTM D570 |
| Linear Mold Shrinkage | 0.0065 cm/cm | 0.0065 in/in | Flow Direction; ASTM D955 |
| Melt Flow | 15 g/10 min @Load 5.00 kg, Temperature 200 °C |
15 g/10 min @Load 11.0 lb, Temperature 392 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore D | 67 - 77 | 67 - 77 | ASTM D2240 |
| Tensile Strength, Yield | 30.0 MPa | 4350 psi | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 33.0 MPa | 4790 psi | chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 1.502 GPa | 217.8 ksi | chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched (ISO) | 3.50 kJ/m² | 1.67 ft-lb/in² | ISO-180 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 0.46 MPa (66 psi) | 81.0 °C | 178 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 67.0 °C | 153 °F | ASTM D648 |
| Vicat Softening Point | 90.0 °C @Load 1.00 kg, Thickness 3.17 mm |
194 °F @Load 2.20 lb, Thickness 0.125 in |
ASTM D1525 |
| Optical Properties | Metric | English | Comments |
|---|---|---|---|
| Transmission, Visible | 90 % | 90 % | ASTM D1003 |