Diamond Polymers PC 2109E UV Natural - Extrusion Grade, UV Stabilized, Flame Retardant Polycarbonate

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Extruded , Polycarbonate, Unreinforced, Flame Retardant , Polycarbonate, UV Stabilized
Manufacturer Diamond and Network Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers PC 2109E UV Natural - Extrusion Grade, UV Stabilized, Flame Retardant Polycarbonate.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.23 g/cc
1.23 g/cc
ASTM D792
Water Absorption 0.15 %

@Temperature 23.0 °C,
Time 86400 sec
0.15 %

@Temperature 73.4 °F,
Time 24.0 hour
ASTM D570
Linear Mold Shrinkage 0.0020 - 0.0070 cm/cm
0.0020 - 0.0070 in/in
ASTM D955
Melt Flow 6.0 g/10 min

@Load 1.20 kg,
Temperature 300 °C
6.0 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 120
120
ASTM D785
Tensile Strength, Yield 61.3 MPa
8890 psi
chs 2.0 in/min; ASTM D638
Flexural Strength 90.1 MPa
13100 psi
chs 0.05 in/min; 5% strain; ASTM D790
Flexural Modulus 2.205 GPa
319.8 ksi
chs 0.05 in/min; ASTM D790
Izod Impact, Notched 7.47 J/cm

@Thickness 3.17 mm
14.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 123 °C
253 °F
0.125";; ASTM D648
Vicat Softening Point 150 °C

@Load 1.00 kg,
Thickness 3.17 mm
302 °F

@Load 2.20 lb,
Thickness 0.125 in
ASTM D1525
Flammability, UL94 5VB

@Thickness 1.57 mm
5VB

@Thickness 0.0620 in
5VA

@Thickness 3.17 mm
5VA

@Thickness 0.125 in