Diamond Polymers PC 1035L Impact Modified, Polycarbonate, Injection Molding Grade

Category Polymer , Thermoplastic , Polycarbonate (PC) , Polycarbonate, Impact Modified
Manufacturer Diamond and Network Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers PC 1035L Impact Modified, Polycarbonate, Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.20 g/cc
1.20 g/cc
ASTM D792
Melt Flow 12 g/10 min

@Load 1.20 kg,
Temperature 300 °C
12 g/10 min

@Load 2.65 lb,
Temperature 572 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 59.1 MPa
8570 psi
chs 2.0 in/min; ASTM D638
Flexural Strength 82.4 MPa
12000 psi
chs 0.05 in/min; 5% strain; ASTM D790
Flexural Modulus 2.246 GPa
325.8 ksi
chs 0.05 in/min; ASTM D790
Izod Impact, Notched 6.94 J/cm

@Thickness 3.17 mm
13.0 ft-lb/in

@Thickness 0.125 in
ASTM D256
Thermal Properties Metric English Comments
Deflection Temperature at 1.8 MPa (264 psi) 122 °C
252 °F
0.125";; ASTM D648
Vicat Softening Point 146 °C

@Load 1.00 kg,
Thickness 3.17 mm
295 °F

@Load 2.20 lb,
Thickness 0.125 in
ASTM D1525