Diamond Polymers ABS/PC FC-30
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABS/PC FC-30.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Description: Injection Molding Grade, High Impact, Flame RetardantInformation provided by Diamond Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | ASTM D792 |
| Linear Mold Shrinkage | 0.0040 - 0.0060 cm/cm | 0.0040 - 0.0060 in/in | ASTM D955 |
| Melt Flow | 1.5 g/10 min @Load 5.00 kg, Temperature 200 °C |
1.5 g/10 min @Load 11.0 lb, Temperature 392 °F |
Procedure A Condition G; ASTM D1238 |
| 7.5 g/10 min @Load 3.80 kg, Temperature 230 °C |
7.5 g/10 min @Load 8.38 lb, Temperature 446 °F |
Procedure A Condition I; ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Rockwell R | 117 | 117 | ASTM D785 |
| Tensile Strength, Yield | 55.2 MPa | 8000 psi | chs 2 in/min; ASTM D638 |
| Flexural Modulus | 2.66 GPa | 386 ksi | Tangent, chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 5.87 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
11.0 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
bar; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Deflection Temperature at 1.8 MPa (264 psi) | 98.9 °C | 210 °F | 0.125 in bar Unannealed/Conditioned 40 hours at 23°C; ASTM D648 |
| 116 °C | 240 °F | 0.125 in bar Annealed 4 hours at 80°C; ASTM D648 | |
| Vicat Softening Point | 125 °C | 257 °F | 0.125 inch, 1 Kg; ASTM D1525 |
| Flammability, UL94 | V-0 | V-0 | 0.100 in |
| V-2 @Thickness 0.930 mm |
V-2 @Thickness 0.0366 in |
||
| V-0 @Thickness 1.50 mm |
V-0 @Thickness 0.0591 in |
||
| 5VA @Thickness 2.50 mm |
5VA @Thickness 0.0984 in |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Rear Barrel Temperature | 238 - 257 °C | 460 - 495 °F | |
| Middle Barrel Temperature | 238 - 257 °C | 460 - 495 °F | |
| Front Barrel Temperature | 238 - 254 °C | 460 - 490 °F | |
| Nozzle Temperature | 238 - 254 °C | 460 - 490 °F | |
| Melt Temperature | 227 - 249 °C | 440 - 480 °F | Melt temperatures above 490°F are not recommended for long periods of time which may result in color shifts and or thermal instability. |
| Mold Temperature | 60.0 - 82.2 °C | 140 - 180 °F | Higher mold temperature can aid flow in processing, provides a better surface finish, and creates less residual stress in the finished products. |
| Drying Temperature | 90.6 - 98.9 °C | 195 - 210 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | |
| Moisture Content | <= 0.10 % | <= 0.10 % | |
| Back Pressure | 0.345 - 0.689 MPa | 50.0 - 100 psi |
Users viewing this material also viewed the following:
- MV Labs DY870 Dy2(C2O4)3·xH2O Dysprosium oxalate hydrate
- NanoAmor 95%, OD: 20-30 nm COOH Functionalized Aligned Multi-Walled Carbon Nanotubes
- PolyOne Geon™ Vinyl Flexible B80MB Polyvinyl Chloride, Flexible (PVC, Flexible)
- Materion Beryllium Copper Alloy M25 Wire; 1/2HT (TH02) Temper; 1.3-12.7 mm Diameter (UNS C17300)
- Karina E 80/321-IS-RG Clear PVC Compound
- Cadi 10 MOLD-MOR™
- ExxonMobil Escorene® HD-8660 LHDPE Rotational Molding Grade (discontinued **)
- DuPont Performance Polymers Delrin® SC631 NC010 Acetal (POM) (Unverified Data**)
- Polykemi AB POLYelast TPE Z557 Thermoplastic Elastomer, SEBS-based
- DuPont Performance Polymers Zytel® HTN FE8200 NC010 Polyphthalamide (PPA) (Unverified Data**)
Copyright © lookpolymers.com All Rights Reserved