- Diamond Polymers ABSPC 9802 ABS/PC Molding Grade, High Impact, High Heat
Diamond Polymers ABSPC 9802 ABS/PC Molding Grade, High Impact, High Heat
| Category | Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC) |
| Manufacturer | Diamond and Network Polymers |
| Trade Name | |
| Port | Shanghai port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Diamond Polymers ABSPC 9802 ABS/PC Molding Grade, High Impact, High Heat.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.16 g/cc | 1.16 g/cc | ASTM D792 |
| Melt Flow | 28 g/10 min @Load 5.00 kg, Temperature 265 °C |
28 g/10 min @Load 11.0 lb, Temperature 509 °F |
ASTM D1238 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Tensile Strength, Yield | 55.1 MPa | 7990 psi | chs 2.0 in/min; ASTM D638 |
| Elongation at Yield | 4.7 % | 4.7 % | chs 2.0 in/min; ASTM D638 |
| Flexural Strength | 86.8 MPa | 12600 psi | chs 0.05 in/min; ASTM D790 |
| Flexural Modulus | 2.274 GPa | 329.8 ksi | tangent; chs 0.05 in/min; ASTM D790 |
| Izod Impact, Notched | 5.43 J/cm @Thickness 3.17 mm, Temperature 23.0 °C |
10.2 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F |
ASTM D256 |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Vicat Softening Point | 142 °C @Load 1.00 kg, Thickness 3.17 mm |
288 °F @Load 2.20 lb, Thickness 0.125 in |
ASTM D1525 |