Diamond Polymers ABSPC 7430-1005T ABS/PC Injection Molding Grade

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Diamond and Network Polymers
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers ABSPC 7430-1005T ABS/PC Injection Molding Grade.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.13 g/cc
1.13 g/cc
ASTM D792
Melt Flow 10 g/10 min

@Load 10.0 kg,
Temperature 220 °C
10 g/10 min

@Load 22.0 lb,
Temperature 428 °F
ASTM D1238
Mechanical Properties Metric English Comments
Tensile Strength, Yield 51.0 MPa
7400 psi
chs 5 mm/min; ASTM D638
Elongation at Break 130 %
130 %
chs 5 mm/min; ASTM D638
Flexural Strength 77.2 MPa

@Thickness 6.35 mm
11200 psi

@Thickness 0.250 in
tangent; chs 2.5 in/min; 100 mm SL; ASTM D790
Flexural Modulus 2.274 GPa

@Thickness 6.35 mm
329.8 ksi

@Thickness 0.250 in
tangent; chs 2.5 in/min; 100 mm SL; ASTM D790
Izod Impact, Notched 2.03 J/cm

@Thickness 6.35 mm,
Temperature -30.0 °C
3.80 ft-lb/in

@Thickness 0.250 in,
Temperature -22.0 °F
ASTM D256
4.32 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
8.09 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 136 °C

@Load 1.00 kg
277 °F

@Load 2.20 lb
120°C/hr; ASTM D1525