Diamond Polymers ABSPC 7030-HES ABS/PC Injection Molding Grade, High Impact

Category Polymer , Thermoplastic , ABS Polymer , Polycarbonate/ABS Alloy, Unreinforced , Polycarbonate (PC)
Manufacturer Diamond and Network Polymers
Trade Name
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Diamond Polymers ABSPC 7030-HES ABS/PC Injection Molding Grade, High Impact.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Information Provided by Diamond Polymers, Inc. & Network Polymers, Inc.
Physical Properties Metric English Comments
Specific Gravity 1.14 g/cc
1.14 g/cc
ASTM D792
Linear Mold Shrinkage 0.0040 - 0.0060 cm/cm
0.0040 - 0.0060 in/in
ASTM D955
Melt Flow 12.8 g/10 min

@Load 10.0 kg,
Temperature 220 °C
 12.8 g/10 min

@Load 22.0 lb,
Temperature 428 °F
 ASTM D1238
Mechanical Properties Metric English Comments
Hardness, Rockwell R 105
105
ASTM D785
Tensile Strength, Yield 55.0 MPa
7980 psi
chs 5 mm/min; ASTM D638
Elongation at Break 70 %
70 %
chs 5 mm/min; ASTM D638
Flexural Strength 93.7 MPa

@Thickness 6.35 mm
 13600 psi

@Thickness 0.250 in
 tangent; chs 2.5 in/min; 100 mm SL; ASTM D790
Flexural Modulus 2.412 GPa

@Thickness 6.35 mm
 349.8 ksi

@Thickness 0.250 in
 tangent; chs 2.5 in/min; 100 mm SL; ASTM D790
Izod Impact, Notched 1.50 J/cm

@Thickness 6.35 mm,
Temperature -30.0 °C
 2.81 ft-lb/in

@Thickness 0.250 in,
Temperature -22.0 °F
 ASTM D256
4.81 J/cm

@Thickness 6.35 mm,
Temperature 23.0 °C
 9.01 ft-lb/in

@Thickness 0.250 in,
Temperature 73.4 °F
 ASTM D256
Thermal Properties Metric English Comments
Vicat Softening Point 125 °C

@Load 1.00 kg
 257 °F

@Load 2.20 lb
 120°C/hr; ASTM D1525