Denka REOMER G G8250 Thermoplastic Elastomer, For Injection Molding

Category Polymer , Thermoplastic , Elastomer, TPE
Manufacturer Denka
Trade Name
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Denka REOMER G G8250 Thermoplastic Elastomer, For Injection Molding.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Essentially a thermoplastic elastomer with the characteristics of PVC resin and rubber, with excellent rubber-like elasticity. Offers excellent rubbery characteristics, such as permanent compressive distortion, rebound elasticity, etc. compared to soft PVC, and excellent bending strength and ozone resistance compared to rubberApplications[Automotive components]door moldingsweather-stripsglass run channelsside bumpersgasketsmud flapshead restsarm restssteering wheelstrimshift bar bootspedal pads[Construction material, manufacturing article home electric, appliance components]gasketsairtight materialscontainer packingpacking for vacuum cleanershosestubes[For electric wire]appliance cordscabtire
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
JIS-Z-8807
Evaporation Loss 1.0 %
1.0 %
JIS-A-5756
Mechanical Properties Metric English Comments
Hardness, Shore A 50
50
JIS-K-6301
Tensile Strength at Break 9.81 MPa
1420 psi
JIS-K-6723
Elongation at Break 420 %
420 %
JIS-K-6723
100% Modulus 0.002943 GPa
0.4269 ksi
JIS-K-6723
Resilience 52
52
JIS-K-6301
Compression Set 51 %
51 %
JIS-K-6301
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -26.0 °C
-14.8 °F
JIS-K-6723
Descriptive Properties Value Comments
Bending Strength, Times, JIS-K-6301 over 100k
Heating: Retention Rate of Elongation, % 93
100°C x 120 hrs
Heating: Retention Rate of Tensile Strength, % 98
100°C x 120 hrs
Oil Resistance: Retention of Tensile Strength, % 85
JIS-K-6723
Oil Resistance: Retention Rate of Elongation, % 72
JIS-K-6723