Material Notes:
Essentially a thermoplastic elastomer with the characteristics of PVC resin and rubber, with excellent rubber-like elasticity. Offers excellent rubbery characteristics, such as permanent compressive distortion, rebound elasticity, etc. compared to soft PVC, and excellent bending strength and ozone resistance compared to rubberApplications[Automotive components]door moldingsweather-stripsglass run channelsside bumpersgasketsmud flapshead restsarm restssteering wheelstrimshift bar bootspedal pads[Construction material, manufacturing article home electric, appliance components]gasketsairtight materialscontainer packingpacking for vacuum cleanershosestubes[For electric wire]appliance cordscabtire
Physical Properties Metric English Comments
Density 1.33 g/cc
0.0480 lb/in³
JIS-Z-8807
Evaporation Loss 1.9 %
1.9 %
JIS-A-5756
Mechanical Properties Metric English Comments
Hardness, Shore A 79
79
JIS-K-6301
Tensile Strength at Break 15.99 MPa
2319 psi
JIS-K-6723
Elongation at Break 298 %
298 %
JIS-K-6723
100% Modulus 0.0070632 GPa
1.0244 ksi
JIS-K-6723
Resilience 23
23
JIS-K-6301
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -25.0 °C
-13.0 °F
JIS-K-6723
Descriptive Properties Value Comments
Bending Strength, Times, JIS-K-6301 over 100k
Heating: Retention Rate of Elongation, % 95
100°C x 120 hrs
Heating: Retention Rate of Tensile Strength, % 110
100°C x 120 hrs
Oil Resistance: Retention of Tensile Strength, % 101
JIS-K-6723
Oil Resistance: Retention Rate of Elongation, % 88
JIS-K-6723