Daikin NEOFLON RP-4040 EFEP Pellets

Category Polymer , Thermoplastic , Fluoropolymer , ETFE/ECTFE , Modified ETFE, Unreinforced , FEP
Manufacturer Daikin Industries
Trade Name NEOFLON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin NEOFLON RP-4040 EFEP Pellets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NEOFLON EFEP is an ETFE based fluoropolymer combining the excellent physical properties derived from ETFE together with a low processing temperature that is more compatible with conventional thermoplastic polymers. NEOFLON EFEP resins adhere well to many kinds of plastics (nylons, EVOH, modified PE, ETFE) and inorganic materials (glass, metals) without adhesive or etching. These resins have a very high transparency and are suitable for extrusion and co-extrusion, injection molding and blow molding applications.Processing Methods: Extrusion, blow molding.Applications: Transparent tubing, pipes, bottles, containers, etc.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.74 g/cc
1.74 g/cc
at 25°C
Water Absorption <= 0.10 %

@Thickness 8.50 mm,
Time 86400 sec
<= 0.10 %

@Thickness 0.335 in,
Time 24.0 hour
ASTM D570
Oxygen Transmission 70.0 cc-mm/m²-24hr-atm
178 cc-mil/100 in²-24hr-atm
at 25°C
Nitrogen Transmission 20.0 cc-mm/m²-24hr-atm
50.8 cc-mil/100 in²-24hr-atm
at 25°C
Viscosity 1.00e+6 - 1.00e+7 cP

@Temperature 300 - 330 °C
1.00e+6 - 1.00e+7 cP

@Temperature 572 - 626 °F
Melt viscosity
Linear Mold Shrinkage 0.030 - 0.040 cm/cm
0.030 - 0.040 in/in
Melt Flow 3.0 - 8.0 g/10 min
3.0 - 8.0 g/10 min
Deformation 2.3 %
2.3 %
13.7 MPa load, at 25°C, 24 hrs; ASTM D621
5.4 %
5.4 %
6.7 MPa load, at 100°C, 24 hrs; ASTM D621
Mechanical Properties Metric English Comments
Hardness, Shore D 75
75
Tensile Strength at Break 40.0 - 50.0 MPa
5800 - 7250 psi
ASTM D638
Elongation at Break 420 - 460 %
420 - 460 %
ASTM D638
Tensile Modulus 0.490 - 0.784 GPa
71.1 - 114 ksi
ASTM D638
Flexural Modulus 0.882 - 1.372 GPa
128 - 199.0 ksi
ASTM D790
Compressive Strength 11.0 MPa

@Temperature 25.0 °C
1600 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Izod Impact, Unnotched NB
NB
ASTM D256
Coefficient of Friction 0.055 - 0.078
0.055 - 0.078
Coefficient of Friction, Static 0.060
0.060
Coated-steel surface
Taber Abrasion, mg/1000 Cycles <= 139.2
<= 139.2
9.8 N load, cs-10 wheel
Thermal Properties Metric English Comments
CTE, linear 50.0 - 90.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
27.8 - 50.0 µin/in-°F

@Temperature 73.4 - 140 °F
ASTM D696
Thermal Conductivity 0.240 W/m-K
1.67 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 160 °C
320 °F
Maximum Service Temperature, Air 150 °C
302 °F
Continuous use
Flammability, UL94 V-0
V-0
Oxygen Index 31 %
31 %
ASTM D2863
Optical Properties Metric English Comments
Transmission, Visible 90 %
90 %
transparent; thickness not quantified
Electrical Properties Metric English Comments
Volume Resistivity <= 1.00e+16 ohm-cm
<= 1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 2.6

@Frequency 1000 Hz
2.6

@Frequency 1000 Hz
ASTM D150
2.6

@Frequency 1e+6 Hz
2.6

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 16.0 kV/mm

@Thickness 3.20 mm
406 kV/in

@Thickness 0.126 in
Short time; ASTM D149
Dissipation Factor 0.00080

@Frequency 1000 Hz
0.00080

@Frequency 1000 Hz
ASTM D150
0.0050

@Frequency 1e+6 Hz
0.0050

@Frequency 1e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Chemical Resistance Excellent
Contact Angle 96
Angle to level
Weatherability Excellent