Daikin NEOFLON M-300H PCTFE Granular Molding Powder

Category Polymer , Thermoplastic , Fluoropolymer , Polychlorotrifluoroethylene (PCTFE); Molded
Manufacturer Daikin Industries
Trade Name NEOFLON
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin NEOFLON M-300H PCTFE Granular Molding Powder.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NEOFLON PCTFE M-300 series is used for general purpose applications.Description:Granular powders.Processing Methods: Compression molding, extrusion.Uses: Sheets, rods, tubing.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 2.10 - 2.14 g/cc
2.10 - 2.14 g/cc
ASTM D792
Bulk Density 0.950 g/cc
0.0343 lb/in³
Water Absorption 0.00 %

@Thickness 8.50 mm,
Time 86400 sec
0.00 %

@Thickness 0.335 in,
Time 24.0 hour
ASTM D570
Oxygen Transmission 3.00 cc-mm/m²-24hr-atm
7.62 cc-mil/100 in²-24hr-atm
at 25°C
Nitrogen Transmission 0.500 cc-mm/m²-24hr-atm
1.27 cc-mil/100 in²-24hr-atm
at 25°C
Viscosity 1.00e+11 cP

@Temperature 230 °C
1.00e+11 cP

@Temperature 446 °F
Melt viscosity
Linear Mold Shrinkage 0.015 - 0.020 cm/cm
0.015 - 0.020 in/in
Deformation 0.20 %
0.20 %
13.7 MPa load, at 25°C, 24 hrs; ASTM D621
2.6 %
2.6 %
6.7 MPa load, at 100°C, 24 hrs; ASTM D621
Mechanical Properties Metric English Comments
Hardness, Shore D 80
80
Tensile Strength at Break 31.0 - 41.0 MPa
4500 - 5950 psi
ASTM D638
Elongation at Break 80 - 250 %
80 - 250 %
ASTM D638
Tensile Modulus 1.029 - 2.058 GPa
149.2 - 298.5 ksi
ASTM D638
Flexural Modulus 1.274 - 1.764 GPa
184.8 - 255.9 ksi
ASTM D790
Compressive Strength 9.00 - 12.0 MPa

@Temperature 25.0 °C
1310 - 1740 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Izod Impact, Unnotched 1.33 - 1.44 J/cm
2.49 - 2.70 ft-lb/in
ASTM D256
Coefficient of Friction, Static 0.080
0.080
Coated-steel surface
Taber Abrasion, mg/1000 Cycles <= 40.0
<= 40.0
Calculated using estimated density, 9.8 N load, cs-10 wheel
Thermal Properties Metric English Comments
CTE, linear 45.0 - 70.0 µm/m-°C

@Temperature 23.0 - 60.0 °C
25.0 - 38.9 µin/in-°F

@Temperature 73.4 - 140 °F
ASTM D696
Thermal Conductivity 0.200 - 0.220 W/m-K
1.39 - 1.53 BTU-in/hr-ft²-°F
ASTM C177
Melting Point 210 - 212 °C
410 - 414 °F
Maximum Service Temperature, Air 120 °C
248 °F
Continuous use
Flammability, UL94 V-0
V-0
Oxygen Index >= 95 %
>= 95 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity <= 1.00e+16 ohm-cm
<= 1.00e+16 ohm-cm
ASTM D257
Dielectric Constant 2.3 - 2.5

@Frequency 1e+6 Hz
2.3 - 2.5

@Frequency 1e+6 Hz
ASTM D150
2.3 - 2.7

@Frequency 1000 Hz
2.3 - 2.7

@Frequency 1000 Hz
ASTM D150
Dielectric Strength 20.0 - 24.0 kV/mm

@Thickness 3.20 mm
508 - 610 kV/in

@Thickness 0.126 in
Short time; ASTM D149
Dissipation Factor 0.010

@Frequency 1e+6 Hz
0.010

@Frequency 1e+6 Hz
ASTM D150
0.023 - 0.027

@Frequency 1000 Hz
0.023 - 0.027

@Frequency 1000 Hz
ASTM D150
Descriptive Properties Value Comments
Chemical Resistance Excellent
Contact Angle 84
Angle to level
Flow Value 1-3E-3
Measured by flow tester at 230°C, under load 9.8 MPa (nozzle size 1 mm in dia., 1 mm in length)
Weatherability Excellent
Zero Strength Time 200-300 s
ASTM D1430-78, at 250°C