Daikin NEOFLON AP-230ASL PFA Pellets

Category Polymer , Thermoplastic , Fluoropolymer , PFA , Polyperfluoroalkoxyethylene, Molded/Extruded
Manufacturer Daikin Industries
Trade Name NEOFLON
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin NEOFLON AP-230ASL PFA Pellets.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
NEOFLON PFA pellets have good melt flowability, and can be processed in the same manner as other thermoplastic resins.Applications: Anti-static grader for extrusion molded parts. Piping, tube, etc.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 2.12 - 2.17 g/cc
2.12 - 2.17 g/cc
at 25°C
Bulk Density 1.20 g/cc
0.0434 lb/in³
Water Absorption <= 0.010 %

@Thickness 8.50 mm,
Time 86400 sec
<= 0.010 %

@Thickness 0.335 in,
Time 24.0 hour
ASTM D570
Viscosity 1.00e+6 - 1.00e+7 cP

@Temperature 380 °C
1.00e+6 - 1.00e+7 cP

@Temperature 716 °F
Melt viscosity
Linear Mold Shrinkage 0.040 cm/cm
0.040 in/in
Melt Flow 1.0 - 2.5 g/10 min

@Load 5.00 kg,
Temperature 372 °C
1.0 - 2.5 g/10 min

@Load 11.0 lb,
Temperature 702 °F
Deformation 2.4 %
2.4 %
6.7 MPa load, at 100°C, 24 hrs; ASTM D621
2.7 %
2.7 %
13.7 MPa load, at 25°C, 24 hrs; ASTM D621
Mechanical Properties Metric English Comments
Hardness, Shore D 60
60
Tensile Strength at Break 27.0 - 35.0 MPa
3920 - 5080 psi
ASTM D638
Elongation at Break 280 - 400 %
280 - 400 %
ASTM D638
Tensile Modulus 0.451 GPa
65.4 ksi
ASTM D638
Flexural Modulus 0.647 - 0.686 GPa
93.8 - 99.5 ksi
ASTM D790
Compressive Strength 5.00 - 6.00 MPa

@Temperature 25.0 °C
725 - 870 psi

@Temperature 77.0 °F
1% deformation; ASTM D695
Izod Impact, Unnotched NB
NB
ASTM D256
Coefficient of Friction 0.040 - 0.060
0.040 - 0.060
Coefficient of Friction, Static 0.050
0.050
Coated-steel surface
Taber Abrasion, mg/1000 Cycles <= 96.75
<= 96.75
9.8 N load, cs-10 wheel
Thermal Properties Metric English Comments
CTE, linear 120 µm/m-°C

@Temperature 23.0 - 60.0 °C
66.7 µin/in-°F

@Temperature 73.4 - 140 °F
ASTM D696
Melting Point 302 - 310 °C
576 - 590 °F
Maximum Service Temperature, Air 260 °C
500 °F
Continuous use
Flammability, UL94 V-0
V-0
Oxygen Index >= 95 %
>= 95 %
ASTM D2863
Electrical Properties Metric English Comments
Volume Resistivity <= 1.00e+18 ohm-cm
<= 1.00e+18 ohm-cm
ASTM D257
Dielectric Constant 2.1

@Frequency 1000 Hz
2.1

@Frequency 1000 Hz
ASTM D150
2.1

@Frequency 1e+6 Hz
2.1

@Frequency 1e+6 Hz
ASTM D150
Dielectric Strength 20.0 kV/mm

@Thickness 3.20 mm
508 kV/in

@Thickness 0.126 in
Short time; ASTM D149
Dissipation Factor 0.000010

@Frequency 1000 Hz
0.000010

@Frequency 1000 Hz
ASTM D150
0.00030

@Frequency 1e+6 Hz
0.00030

@Frequency 1e+6 Hz
ASTM D150
Descriptive Properties Value Comments
Chemical Resistance Excellent
Contact Angle 115
Angle to level
Weatherability Excellent