Daikin DAI-EL G-763 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-763 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: Excellent mold releasability for O-rings.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.85 g/cc
1.85 g/cc
at 25°C
Mooney Viscosity 29

@Temperature 121 °C
29

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 69
69
Peak value, at 25°C
Tensile Strength at Break 15.0 MPa
2180 psi
Tensile Strength, Yield 3.30 MPa

@Strain 100 %
479 psi

@Strain 100 %
Elongation at Break 240 %
240 %
Tear Strength 22.5 kN/m
128 pli
at 25°C
Compression Set 13 %
13 %
70 hours at 25°C
9.0 %

@Temperature 100 °C
9.0 %

@Temperature 212 °F
70 hours
13 %

@Temperature 175 °C
13 %

@Temperature 347 °F
70 hours
23 %

@Temperature 200 °C
23 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -18.0 °C
-0.400 °F
TR test, TR10
-15.6 °C
3.92 °F
Gehman torsion test, T10
-8.50 °C
16.7 °F
Gehman torsion test, T2
-8.00 °C
17.6 °F
TR test, TR70
Brittleness Temperature -21.0 °C
-5.80 °F
Processing Properties Metric English Comments
Processing Temperature 170 °C
338 °F
Cure Measuring Temperature
Cure Time 3.70 min
0.0617 hour
Curelastmeter