Daikin DAI-EL G-702 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content

Category Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE)
Manufacturer Daikin Industries
Trade Name DAI-EL
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF Daikin DAI-EL G-702 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: General purpose with excellent elongation and tear strength.Information provided by Daikin Industries.
Physical Properties Metric English Comments
Specific Gravity 1.85 g/cc
1.85 g/cc
at 25°C
Mooney Viscosity 32

@Temperature 121 °C
32

@Temperature 250 °F
ML 1+10
Mechanical Properties Metric English Comments
Hardness, Shore A 70
70
Peak value, at 25°C
Tensile Strength at Break 16.4 MPa
2380 psi
Tensile Strength, Yield 3.40 MPa

@Strain 100 %
493 psi

@Strain 100 %
Elongation at Break 300 %
300 %
Tear Strength 23.5 kN/m
134 pli
at 25°C
Taber Abrasion, mg/1000 Cycles 250
250
H-22 abrasive wheel, load: 1000g x 2
Compression Set 20 %
20 %
70 hours at 25°C
11 %

@Temperature 100 °C
11 %

@Temperature 212 °F
70 hours
15 %

@Temperature 175 °C
15 %

@Temperature 347 °F
70 hours
26 %

@Temperature 200 °C
26 %

@Temperature 392 °F
70 hours
Thermal Properties Metric English Comments
Minimum Service Temperature, Air -18.0 °C
-0.400 °F
TR test, TR10
-15.5 °C
4.10 °F
Gehman torsion test, T10
-8.00 °C
17.6 °F
TR test, TR70
-8.00 °C
17.6 °F
Gehman torsion test, T2
Brittleness Temperature -25.0 °C
-13.0 °F
Processing Properties Metric English Comments
Processing Temperature 160 °C
320 °F
Cure Measuring Temperature
Cure Time 4.00 min
0.0667 hour
Curelastmeter