- Daikin DAI-EL G-701 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
Daikin DAI-EL G-701 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content
| Category | Polymer , Thermoset , Fluoropolymer, TS , Thermoset Fluoroelastomer , Rubber or Thermoset Elastomer (TSE) |
| Manufacturer | Daikin Industries |
| Trade Name | DAI-EL |
| Port | Ningbo port,China |
| Trade Terms | FOB, CFR, CIF |
| Payment Terms | L/C, T/T, Western Union |
| Download PDF | Daikin DAI-EL G-701 Fluoroelastomer Copolymer, Bisphenol Curable Grade, 66% Fluorine Content.pdf  |
| Price | EMAIL US sales@lookpolymers.com |
Material Notes:
Offers minimal compression set and excellent sealing. The copolymer type offers good compression set characteristics.Features: General purpose with excellent compression set.Information provided by Daikin Industries.
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.85 g/cc | 1.85 g/cc | at 25°C |
| Mooney Viscosity | 32 @Temperature 121 °C |
32 @Temperature 250 °F |
ML 1+10 |
| Mechanical Properties | Metric | English | Comments |
|---|---|---|---|
| Hardness, Shore A | 73 | 73 | Peak value, at 25°C |
| Tensile Strength at Break | 14.6 MPa | 2120 psi | |
| Tensile Strength, Yield | 5.30 MPa @Strain 100 % |
769 psi @Strain 100 % |
|
| Elongation at Break | 190 % | 190 % | |
| Tear Strength | 19.6 kN/m | 112 pli | at 25°C |
| Taber Abrasion, mg/1000 Cycles | 325 | 325 | H-22 abrasive wheel, load: 1000g x 2 |
| Compression Set | 7.0 % | 7.0 % | 70 hours at 25°C |
| 4.0 % @Temperature 100 °C |
4.0 % @Temperature 212 °F |
70 hours | |
| 11 % @Temperature 175 °C |
11 % @Temperature 347 °F |
70 hours | |
| 17 % @Temperature 200 °C |
17 % @Temperature 392 °F |
70 hours |
| Thermal Properties | Metric | English | Comments |
|---|---|---|---|
| Minimum Service Temperature, Air | -18.0 °C | -0.400 °F | TR test, TR10 |
| -12.5 °C | 9.50 °F | Gehman torsion test, T10 | |
| -9.00 °C | 15.8 °F | TR test, TR70 | |
| -6.00 °C | 21.2 °F | Gehman torsion test, T2 | |
| Brittleness Temperature | -17.0 °C | 1.40 °F |
| Electrical Properties | Metric | English | Comments |
|---|---|---|---|
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm |
| Processing Properties | Metric | English | Comments |
|---|---|---|---|
| Processing Temperature | 170 °C | 338 °F | Cure Measuring Temperature |
| Cure Time | 4.20 min | 0.0700 hour | Curelastmeter |