DSM Stanyl® TW272B6 (PA46+PTFE)-CF30

Category Polymer , Thermoplastic , Nylon , Nylon 46
Manufacturer DSM Engineering Plastics
Trade Name Stanyl®
Port Ningbo port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Stanyl® TW272B6 (PA46+PTFE)-CF30.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Physical Properties Metric English Comments
Density 1.35 g/cc
0.0488 lb/in³
dry; ISO 1183
Moisture Absorption 2.25 %
2.25 %
Sim. To ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
Sim. To ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
0.0060 in/in
Sim. To ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 160 MPa
23200 psi
cond; ISO 527-1/-2
240 MPa
34800 psi
dry; ISO 527-1/-2
90.0 MPa

@Temperature 200 °C
13100 psi

@Temperature 392 °F
ISO 527-1/-2
100 MPa

@Temperature 180 °C
14500 psi

@Temperature 356 °F
ISO 527-1/-2
110 MPa

@Temperature 160 °C
16000 psi

@Temperature 320 °F
ISO 527-1/-2
130 MPa

@Temperature 120 °C
18900 psi

@Temperature 248 °F
ISO 527-1/-2
Elongation at Break 1.6 %
1.6 %
dry; ISO 527-1/-2
3.5 %
3.5 %
cond; ISO 527-1/-2
3.1 %

@Temperature 120 °C
3.1 %

@Temperature 248 °F
ISO 527-1/-2
3.1 %

@Temperature 160 °C
3.1 %

@Temperature 320 °F
ISO 527-1/-2
3.1 %

@Temperature 180 °C
3.1 %

@Temperature 356 °F
ISO 527-1/-2
3.1 %

@Temperature 200 °C
3.1 %

@Temperature 392 °F
ISO 527-1/-2
Tensile Modulus 14.5 GPa
2100 ksi
cond; ISO 527-1/-2
24.0 GPa
3480 ksi
dry; ISO 527-1/-2
10.0 GPa

@Temperature 200 °C
1450 ksi

@Temperature 392 °F
ISO 527-1/-2
10.5 GPa

@Temperature 180 °C
1520 ksi

@Temperature 356 °F
ISO 527-1/-2
11.0 GPa

@Temperature 160 °C
1600 ksi

@Temperature 320 °F
ISO 527-1/-2
12.5 GPa

@Temperature 120 °C
1810 ksi

@Temperature 248 °F
ISO 527-1/-2
Fatigue Strength 57.0 MPa

@# of Cycles 1.00e+7 ,
Temperature 140 °C
8270 psi

@# of Cycles 1.00e+7 ,
Temperature 284 °F
R = 0.1, 8 Hz, dry
66.0 MPa

@# of Cycles 1.00e+6 ,
Temperature 140 °C
9570 psi

@# of Cycles 1.00e+6 ,
Temperature 284 °F
R = 0.1, 8 Hz, dry
76.0 MPa

@# of Cycles 100000 ,
Temperature 140 °C
11000 psi

@# of Cycles 100000 ,
Temperature 284 °F
R = 0.1, 8 Hz, dry
87.0 MPa

@# of Cycles 10000 ,
Temperature 140 °C
12600 psi

@# of Cycles 10000 ,
Temperature 284 °F
R = 0.1, 8 Hz, dry
100 MPa

@# of Cycles 1000 ,
Temperature 140 °C
14500 psi

@# of Cycles 1000 ,
Temperature 284 °F
R = 0.1, 8 Hz, dry
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
23.8 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eU
5.00 J/cm²

@Temperature -30.0 °C
23.8 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eU
5.50 J/cm²

@Temperature -30.0 °C
26.2 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
38.1 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eU
Charpy Impact, Notched 0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
cond; ISO 179/1eA
0.600 J/cm²

@Temperature 23.0 °C
2.86 ft-lb/in²

@Temperature 73.4 °F
dry; ISO 179/1eA
0.600 J/cm²

@Temperature -30.0 °C
2.86 ft-lb/in²

@Temperature -22.0 °F
dry; ISO 179/1eA
1.30 J/cm²

@Temperature 23.0 °C
6.19 ft-lb/in²

@Temperature 73.4 °F
cond; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow 35.0 µm/m-°C
19.4 µin/in-°F
dry; ISO 11359-1/-2
Melting Point 295 °C
563 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
dry; ISO 75-1/-2