Category Polymer , Thermoplastic , Nylon , Nylon 46
Manufacturer DSM Engineering Plastics
Trade Name Stanyl®
Port Shanghai port,China
Trade Terms FOB, CFR, CIF
Payment Terms L/C, T/T, Western Union
Download PDF DSM Stanyl® TW271B6 (PA46+PTFE)-CF30.pdf
Price EMAIL US    sales@lookpolymers.com
  Online Service   lookpolymers   27660005
Material Notes:
30% Carbon Reinforced, Heat Stabilized, Wear and Friction Modified
Physical Properties Metric English Comments
Density 1.32 g/cc
0.0477 lb/in³
dry; ISO 1183
Moisture Absorption 2.40 %
2.40 %
Sim. To ISO 62
Linear Mold Shrinkage, Flow 0.0030 cm/cm
0.0030 in/in
ISO 294-4
Linear Mold Shrinkage, Transverse 0.0070 cm/cm
0.0070 in/in
ISO 294-4
Mechanical Properties Metric English Comments
Tensile Strength, Ultimate 170 MPa
24700 psi
cond; ISO 527-1/-2
260 MPa
37700 psi
dry; ISO 527-1/-2
95.0 MPa

@Temperature 200 °C
 13800 psi

@Temperature 392 °F
 ISO 527-1/-2
105 MPa

@Temperature 180 °C
 15200 psi

@Temperature 356 °F
 ISO 527-1/-2
115 MPa

@Temperature 160 °C
 16700 psi

@Temperature 320 °F
 ISO 527-1/-2
140 MPa

@Temperature 120 °C
 20300 psi

@Temperature 248 °F
 ISO 527-1/-2
Elongation at Break 1.7 %
1.7 %
dry; ISO 527-1/-2
3.5 %
3.5 %
cond; ISO 527-1/-2
3.1 %

@Temperature 120 °C
 3.1 %

@Temperature 248 °F
 ISO 527-1/-2
3.1 %

@Temperature 160 °C
 3.1 %

@Temperature 320 °F
 ISO 527-1/-2
3.1 %

@Temperature 180 °C
 3.1 %

@Temperature 356 °F
 ISO 527-1/-2
3.1 %

@Temperature 200 °C
 3.1 %

@Temperature 392 °F
 ISO 527-1/-2
Tensile Modulus 14.5 GPa
2100 ksi
cond; ISO 527-1/-2
24.0 GPa
3480 ksi
dry; ISO 527-1/-2
11.0 GPa

@Temperature 200 °C
 1600 ksi

@Temperature 392 °F
 ISO 527-1/-2
11.5 GPa

@Temperature 180 °C
 1670 ksi

@Temperature 356 °F
 ISO 527-1/-2
12.0 GPa

@Temperature 160 °C
 1740 ksi

@Temperature 320 °F
 ISO 527-1/-2
13.5 GPa

@Temperature 120 °C
 1960 ksi

@Temperature 248 °F
 ISO 527-1/-2
Fatigue Strength 67.0 MPa

@# of Cycles 1.00e+7 ,
Temperature 140 °C
 9720 psi

@# of Cycles 1.00e+7 ,
Temperature 284 °F
 R = 0.1, 8 Hz, dry
76.0 MPa

@# of Cycles 1.00e+6 ,
Temperature 140 °C
 11000 psi

@# of Cycles 1.00e+6 ,
Temperature 284 °F
 R = 0.1, 8 Hz, dry
86.0 MPa

@# of Cycles 100000 ,
Temperature 140 °C
 12500 psi

@# of Cycles 100000 ,
Temperature 284 °F
 R = 0.1, 8 Hz, dry
97.0 MPa

@# of Cycles 10000 ,
Temperature 140 °C
 14100 psi

@# of Cycles 10000 ,
Temperature 284 °F
 R = 0.1, 8 Hz, dry
110 MPa

@# of Cycles 1000 ,
Temperature 140 °C
 16000 psi

@# of Cycles 1000 ,
Temperature 284 °F
 R = 0.1, 8 Hz, dry
Charpy Impact Unnotched 5.00 J/cm²

@Temperature 23.0 °C
 23.8 ft-lb/in²

@Temperature 73.4 °F
 dry; ISO 179/1eU
5.00 J/cm²

@Temperature -30.0 °C
 23.8 ft-lb/in²

@Temperature -22.0 °F
 dry; ISO 179/1eU
5.50 J/cm²

@Temperature -30.0 °C
 26.2 ft-lb/in²

@Temperature -22.0 °F
 cond; ISO 179/1eU
8.00 J/cm²

@Temperature 23.0 °C
 38.1 ft-lb/in²

@Temperature 73.4 °F
 cond; ISO 179/1eU
Charpy Impact, Notched 0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 cond; ISO 179/1eA
0.700 J/cm²

@Temperature 23.0 °C
 3.33 ft-lb/in²

@Temperature 73.4 °F
 dry; ISO 179/1eA
0.700 J/cm²

@Temperature -30.0 °C
 3.33 ft-lb/in²

@Temperature -22.0 °F
 dry; ISO 179/1eA
1.70 J/cm²

@Temperature 23.0 °C
 8.09 ft-lb/in²

@Temperature 73.4 °F
 cond; ISO 179/1eA
Thermal Properties Metric English Comments
CTE, linear, Parallel to Flow 25.0 µm/m-°C
13.9 µin/in-°F
dry; ISO 11359-1/-2
CTE, linear, Transverse to Flow 35.0 µm/m-°C
19.4 µin/in-°F
dry; ISO 11359-1/-2
Melting Point 295 °C
563 °F
10°C/min; ISO 11357-1/-3
Deflection Temperature at 1.8 MPa (264 psi) 290 °C
554 °F
dry; ISO 75-1/-2